High-impact antistatic PMMA (polymethyl methacrylate) composition as well as preparation method and application thereof
A composition and antistatic technology, which is applied in the field of high impact and antistatic PMMA composition and its preparation, can solve the problems of poor antistatic performance and poor toughness, achieve excellent toughness, excellent antistatic performance, avoid rigidity and Transparency drop effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example
[0054] Example 1 to 17
[0055] Examples 1 to 17 provide a PMMA composition, the component content is shown in Table 1, the preparation method is as follows:
[0056] After mixing the components according to Table 1, they are added to the twin screw extruder, and the PMMA composition is obtained by melting and mixing and extruding granulation;
[0057] The temperature of the twin screw machine extruder is 120 to 170 °C in the first to second zone, 160 to 180 °C in the third to fifth zone, and 170 to 190 °C in the sixth to tenth zone.
[0058] Table 1 Composition content of PMMA composition of Examples 1 to 17 (by weight)
[0059]
Example
[0060] The proportion is 1 to 7
[0061] To provide a PMMA composition for a ratio of 1 to 7, the component content is shown in Table 2, the preparation method is the same as the embodiment.
[0062] Table 2 Component content (by weight) of PMMA composition with a proportion of 1 to 7
[0063]
[0064] Performance testing
[0065] The above embodiment and the performance test of the PMMA composition prepared in proportion, the specific method is as follows:
[0066] Surface resistivity: the PMMA composition is injection molded into a 100×100mm square plate, the test voltage is 100V, and the test is carried out in accordance with IEC60093-1980 standards;
[0067] Light transmittance: the PMMA composition is injection molded into a 2.0mm thickness square plate, tested according to GB / T2410-2008 standards, and the test light is visible;
[0068] Notched impact strength: tested according to ISO 180-2000 standard;
[0069] The test results of Example 1 to 17 are shown in Table 3, and...
PUM
Property | Measurement | Unit |
---|---|---|
Surface resistivity | aaaaa | aaaaa |
Notched impact strength | aaaaa | aaaaa |
The melt flow rate | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap