Rubber composition for shoe sole, application of rubber composition, vulcanized rubber, and preparation method and application of vulcanized rubber

A rubber composition and a technology for the composition, which are used in the preparation of shoe soles, vulcanized rubber, and the field of preparing vulcanized rubber, can solve the problems of low rubber strength and poor flexural resistance, and achieve wear resistance and flexural resistance. Good, high-strength effect

Pending Publication Date: 2022-05-06
CHINA PETROLEUM & CHEM CORP +1
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the defects of low rubber strength, wear resistance and poor flex resistance when the rubber composition provided by the prior art is used to prepare shoe soles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber composition for shoe sole, application of rubber composition, vulcanized rubber, and preparation method and application of vulcanized rubber
  • Rubber composition for shoe sole, application of rubber composition, vulcanized rubber, and preparation method and application of vulcanized rubber
  • Rubber composition for shoe sole, application of rubber composition, vulcanized rubber, and preparation method and application of vulcanized rubber

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0088] Preparation Example 1: Preparation of Vulcanized Rubber

[0089] First mixing:

[0090] Put the main rubber into the internal mixer, set the rotational speed of the internal mixer to 80rpm, and set the mastication temperature of the internal mixer to perform mastication to obtain the masticated rubber. Then white carbon black, additives and surface modifiers are added into the internal mixer, the mixing temperature of the internal mixer is set, and the first mixing is carried out with the above-mentioned masticated rubber to obtain the first mixed rubber.

[0091] Second mixing:

[0092] Lift the top pin of the internal mixer for the first mixing, carry out the second mixing with zinc methacrylate, hydrogenated terpene resin, activator, anti-aging agent, softener and the first mixing rubber, discharge and Parked for 4h to obtain the second rubber compound.

[0093] The third mixing:

[0094] Put the aforementioned second compounded rubber in the internal mixer for m...

preparation example 12

[0098] Second mixing:

[0099] Put the main rubber into the internal mixer, set the rotational speed of the internal mixer to 80rpm, and set the mastication temperature of the internal mixer to perform mastication to obtain the masticated rubber. Then add white carbon black, additives, surface modifiers, zinc methacrylate, hydrogenated terpene resins, activators, anti-aging agents and softeners into the internal mixer, set the mixing temperature of the internal mixer, and plasticize The rubber is mixed for the second time to obtain the second mixed rubber.

[0100] The third mixing:

[0101] Put the aforementioned second compounded rubber in the internal mixer for mastication, set the speed of the internal mixer to 80rpm, and the initial plasticating temperature of the internal mixer to 40°C. After the second compounded rubber is masticated for 1 min, add The vulcanizing agent and the accelerator are mixed for the third time to obtain the final compound.

[0102] The above-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of rubber, and discloses a rubber composition for shoe soles, application of the rubber composition, vulcanized rubber and a preparation method and application of the vulcanized rubber. The rubber composition comprises main rubber, white carbon black, zinc methacrylate, a surface modifier, hydrogenated terpene resin, an activating agent, a softening agent, a vulcanizing agent, an accelerant, an anti-aging agent and an additive, the main body rubber is a combination of butadiene styrene rubber and butadiene rubber, and the additive is calcium sulfate whisker or anhydrite. The vulcanized rubber prepared from the rubber composition provided by the invention has relatively high tensile strength, wear resistance and flexing resistance.

Description

technical field [0001] The invention relates to the field of rubber, in particular to a rubber composition for shoe soles and its application, a method for preparing vulcanized rubber, and the vulcanized rubber prepared by the method and the application of the vulcanized rubber in the preparation of shoe soles. Background technique [0002] Shoes are the necessities of people's life, and the sole is an important factor affecting the quality of shoes. At present, the main materials of sole materials mainly include TPR, EVA, rubber, polyurethane, etc. [0003] In the prior art, white fillers are widely used in footwear products, especially in light-colored or colored products, which can endow the sole with good wear resistance, anti-skid performance and shoe surface adhesion performance, among which white carbon black is the most widely used , but the surface of silica contains polar groups, which has poor compatibility with rubber substrates and has an adverse effect on the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/00C08L9/06C08L45/00C08K7/26C08K5/098C08K3/22C08K5/09C08K7/08C08K13/04A43B13/04
CPCC08L9/00C08L9/06A43B13/04C08K2003/2296C08L2205/035C08L45/00C08K7/26C08K5/098C08K3/22C08K5/09C08K7/08C08K13/04Y02T10/86
Inventor 王雷雷王丽静
Owner CHINA PETROLEUM & CHEM CORP
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com