Converter trunnion area furnace lining erosion part maintenance method and use method after maintenance

A furnace lining erosion and trunnion technology is applied in the field of converter furnace condition maintenance technology, which can solve the problems affecting the maintenance effect of the furnace lining erosion part in the trunnion area of ​​the converter, the high frequency of gunning operations, and the easy falling off of furnace repair bricks, so as to avoid the furnace machine. Matching contradictions, safe and reliable cost, and the effect of reducing the frequency of spraying

Active Publication Date: 2022-06-24
MAANSHAN IRON & STEEL CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the existing technical problems such as difficulty in maintaining the eroded part of the lining in the trunnion area of ​​the converter, high frequency of gunning operations, high consumption of refractory materials, and poor maintenance effect, the purpose of the present invention is to provide a maintenance method for the eroded part of the lining in the trunnion area of ​​the converter and The method of use after maintenance can effectively enhance the maintenance effect of the eroded part of the lining of the converter trunnion area, improve the service life of the converter lining, and reduce the consumption of refractory materials and labor intensity
[0008] In order to solve the problem in the prior art that the patched furnace bricks are easy to fall off, thereby affecting the maintenance effect of the eroded part of the furnace lining in the trunnion area of ​​the converter, the technical solution adopted by the present invention is as follows:

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Converter trunnion area furnace lining erosion part maintenance method and use method after maintenance
  • Converter trunnion area furnace lining erosion part maintenance method and use method after maintenance
  • Converter trunnion area furnace lining erosion part maintenance method and use method after maintenance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] like figure 1 As shown, in this embodiment, a method for maintaining the eroded part of the furnace lining in the trunnion area of ​​the converter and a method for using it after maintenance, specifically:

[0050] (1) 1 furnace of steel before tiling and maintenance, the steel tapping is completed, the steel tapping volume is 68.2t, after the converter is normally splashed with slag to protect the furnace, the slag in the furnace is cleaned. Use a laser thickness gauge to measure the lining thickness of the converter feeding side and the left and right trunnion areas. The measured lining thicknesses of the converter feeding side, left trunnion area and right trunnion area are respectively: 497mm, 538mm and 530mm, that is, the standard value of 650mm for the new lining In comparison, 153mm, 112mm and 120mm were eaten respectively.

[0051] (2) Put 3.5t of clean bar scrap into the slag replenishment hopper, control the amount of slag remaining in the subsidized furnace ...

Embodiment 2

[0059] like figure 1 As shown, in this embodiment, a method for maintaining the eroded part of the furnace lining in the trunnion area of ​​the converter and a method for using it after maintenance, specifically:

[0060] (1) 1 furnace of steel before tiling and maintenance, the steel tapping is completed, the steel tapping volume is 68.1t, and the slag in the furnace is cleaned after the converter is normally splashed with slag to protect the furnace. Use a laser thickness gauge to measure the lining thickness of the converter feeding side and the left and right trunnion areas. The measured lining thicknesses of the converter feeding side, left trunnion area and right trunnion area are: 499mm, 438mm and 396mm respectively, that is, the standard value of 650mm for the new lining In comparison, 151mm, 212mm and 254mm were eaten respectively.

[0061] (2) Put 3.6t of clean bar steel scrap into the slag replenishment hopper, control the amount of slag remaining in the subsidized...

Embodiment 3

[0069] like figure 1 As shown, in this embodiment, a method for maintaining the eroded part of the furnace lining in the trunnion area of ​​the converter and a method for using it after maintenance, specifically:

[0070] (1) 1 furnace of steel before tiling and maintenance, the steel tapping is completed, and the steel tapping volume is 68.6t. Use a laser thickness gauge to measure the lining thickness of the converter feeding side and the left and right trunnion areas. The measured lining thicknesses of the converter feeding side, left trunnion area and right trunnion area are respectively: 429mm, 418mm and 405mm, that is, the standard value of 650mm for the new lining In comparison, 221mm, 232mm and 245mm were eaten respectively.

[0071] (2) Add 4.5t of clean bar scrap steel into the slag replenishment hopper, control the amount of slag remaining in the subsidized furnace converter at 5.4t, prepare 30 repair bricks, and the weight of repair bricks is 10kg / block.

[0072]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a maintenance method for a converter trunnion area furnace lining erosion part and a use method after maintenance, and belongs to the technical field of converter condition maintenance processes. The maintenance method comprises the following steps: measuring the thickness of the converter lining at the charging side and the trunnion area of the converter, and determining the slag remaining amount of the converter and the using amount of slag repair bar scrap steel and fettling bricks; carrying out slag repair on the charging side furnace lining by using the slag repair bar scrap steel; performing tiling maintenance on the furnace lining at the eroded part of the trunnion area by using fettling bricks; and after tiling is finished, a magnesium gunning material is used for gunning the converter trunnion area furnace lining subjected to tiling maintenance. The use method of the maintained converter trunnion area furnace lining erosion part is that the first furnace adopts a full-amount molten iron or magnetic separation slag recycling smelting operation mode. The maintenance effect of the converter trunnion area converter lining erosion part can be enhanced, the service life of the converter lining is prolonged, and refractory material consumption and labor intensity are reduced.

Description

technical field [0001] The invention belongs to the technical field of converter furnace condition maintenance technology, and more specifically relates to a method for maintaining an eroded part of a furnace lining in a trunnion area of ​​a converter and a use method after maintenance, which can realize effective maintenance of the eroded part of a furnace lining in a trunnion area of ​​a converter. Background technique [0002] The service life of the converter lining is of great significance for improving production efficiency, increasing furnace life, improving molten steel quality, improving variety structure, reducing refractory consumption, and increasing economic benefits. The converter lining is mainly composed of insulation layer, permanent layer and working layer. During the smelting process, the converter lining is eroded by a series of strong mechanical, physical and chemical effects, especially the high temperature peroxidized slag has a greater erosion effect ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21C5/44G01B11/06
CPCC21C5/441G01B11/06Y02P10/20
Inventor 邓南阳潘军周军赵滨刘威
Owner MAANSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products