Method for comprehensively utilizing water-based rock debris through SiC template method
A template method and cuttings technology, applied in the field of environmental protection and resource recycling, can solve environmental pollution and other problems, achieve the effect of solving environmental pollution problems, increasing content, and improving mechanical properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0029] Example 1 (comparative example):
[0030] A method for comprehensive utilization of water-based cuttings, the detailed steps of the comprehensive utilization method are as follows:
[0031] a. Using water-based cuttings A and water-based cuttings B as raw materials, 100kg of water-based cuttings A and 10 kg of water-based cuttings B are batched. After batching, a ball mill is used for mixing. During the mixing process, the speed of the ball mill is 200r / min, time is 24h, after ball milling and mixing, the mixed powder is obtained;
[0032] b, adding the mixed powder obtained in step a into a round pot granulator for spray granulation, the frequency of the round pot granulator is 50Hz, and the rotating speed is 25~30r / min; the particle size obtained after granulation is 20 / 140 purpose materials;
[0033] c. The material obtained in step b is dried in a blast drying oven, and the drying temperature is 80° C., and is dried until the moisture content of the obtained prod...
Embodiment 2
[0036] The present invention comprehensively utilizes the method for water-based cuttings through the SiC template method, and the detailed steps of the comprehensive utilization method are as follows:
[0037] a. Using water-based cuttings A and water-based cuttings B as raw materials, and SiC crystal seeds as templates, 100 kg of water-based cuttings A, 10 kg of water-based cuttings B and 2 kg of SiC crystal seeds are batched. Mixing, in the mixing process, the speed of the ball mill is 260r / min, the ball milling time is 20h, and the mixed powder is obtained after the ball milling and mixing;
[0038] b, adding the mixed powder obtained in step a into a round pot granulator for spray granulation, the frequency of the round pot granulator is 50Hz, and the rotating speed is 20~25r / min; the particle size obtained after granulation is 20 / 140 purpose materials;
[0039] c. The material obtained in step b is dried in a blast drying oven, and the drying temperature is 70° C., and ...
Embodiment 3
[0042] The present invention comprehensively utilizes the method for water-based cuttings through the SiC template method, and the detailed steps of the comprehensive utilization method are as follows:
[0043] a. Using water-based cuttings A and water-based cuttings B as raw materials, and SiC crystal seeds as templates, 100 kg of water-based cuttings A, 10 kg of water-based cuttings B and 4 kg of SiC crystal seeds are batched, and after batching, a ball mill is used to carry out Mixing, in the mixing process, the speed of the ball mill is 180r / min, the ball milling time is 32h, and the mixed powder is obtained after the ball milling and mixing;
[0044] b, adding the mixed powder obtained in step a into a round pot granulator for spray granulation, the frequency of the round pot granulator is 50Hz, and the rotating speed is 20~25r / min; the particle size obtained after granulation is 20 / 140 purpose materials;
[0045] c. The material obtained in step b is dried in a blast dr...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
| crush indicators | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
Login to View More