Anti-fatigue and corrosion-resistant forged Al-Mg-Si-Zr aluminum alloy wheel and preparation method thereof

A technology for corrosion-resistant aluminum alloys and aluminum alloys, applied in the field of forging aluminum alloys, can solve the problems of poor corrosion resistance and fatigue resistance, and achieve the effects of enhancing fatigue resistance and corrosion resistance, avoiding fatigue cracks, and improving hardness

Pending Publication Date: 2022-08-09
山东骏程金属科技有限公司 +1
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problems existing in the application process of automobile wheels in the prior art, the purpose of the present invention is to solve the problems of poor fatigue resistance and poor corrosion resistance in the actual application process of automobile wheels, and to provide an anti-fatigue and corrosion-resistant Forged Al-Mg-Si-Zr aluminum alloy wheels

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-fatigue and corrosion-resistant forged Al-Mg-Si-Zr aluminum alloy wheel and preparation method thereof
  • Anti-fatigue and corrosion-resistant forged Al-Mg-Si-Zr aluminum alloy wheel and preparation method thereof
  • Anti-fatigue and corrosion-resistant forged Al-Mg-Si-Zr aluminum alloy wheel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039]An anti-fatigue and anti-corrosion forged Al-Mg-Si-Zr aluminum alloy wheel, the element composition is: Si: 0.70%, Mg: 1.1%, Cu: 0.28%, Fe: 0.21%, Mn: 0.12%, Cr: 0.3%, Ti: 0.02%, Zr: 0.08% and balance Al.

[0040] The specific implementation method is as follows:

[0041] (1) Ingredients: Weigh pure aluminum water, pure aluminum ingot, aluminum-silicon alloy ingot, pure magnesium ingot, pure copper ingot, pure zinc ingot, aluminum-zirconium alloy ingot, aluminum-titanium alloy ingot and aluminum-titanium ingot according to the mass percentage of the elements. Boron wire is smelted to obtain aluminum alloy melt;

[0042] (2) Preparation of round cast rods: Preparation of round cast rods: the aluminum alloy melt is set at 750℃-780℃, the casting speed is 35mm / min~60mm / min, the cooling water strength is 0.04MPa~0.08MPa and the cooling water temperature is Under the condition of 20℃~40℃, cast into a round cast rod with a diameter of 254mm and a length of 6000mm;

[0043] (...

Embodiment 2

[0055] An anti-fatigue and anti-corrosion forged Al-Mg-Si-Zr aluminum alloy wheel, the element composition is: Si: 0.78%, Mg: 1.15%, Cu: 0.32%, Fe: 0.24%, Mn: 0.13%, Cr: 0.25%, Ti: 0.05%, Zr: 0.12% and balance Al.

[0056] The preparation method is the same as in Example 1

Embodiment 3

[0058] An anti-fatigue and anti-corrosion forged Al-Mg-Si-Zr aluminum alloy wheel, the element composition is: Si: 0.75%, Mg: 1.13%, Cu: 0.30%, Fe: 0.22%, Mn: 0.12%, Cr: 0.26%, Ti: 0.03%, Zr: 0.10% and balance Al.

[0059] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of forged aluminum alloy, and particularly relates to an anti-fatigue and corrosion-resistant forged Al-Mg-Si-Zr aluminum alloy wheel and a preparation method thereof. The aluminum alloy wheel is composed of Si, Mg, Cu, Fe, Mn, Cr, Ti, Zr and the balance Al. The aluminum alloy material is forged by optimizing alloy components, carrying out graded homogenization treatment on a cast rod and adopting an optimized aluminum rod heating process and a solid solution and aging process after die forging, the fatigue performance can be circulated for about 7 * 107 weeks under the pressure of 200 Mpa, and the stripping corrosion resistance reaches the PA level. In addition, the tumbling process and the surface treatment process are added, the fatigue resistance and the corrosion resistance of the aluminum alloy wheel are further enhanced, the requirement of a wheel biaxial fatigue test is met, and the requirement of an international first-class main engine plant is met.

Description

technical field [0001] The invention belongs to the technical field of forged aluminum alloys, in particular to a fatigue-resistant and corrosion-resistant forged Al-Mg-Si-Zr aluminum alloy wheel and a preparation method thereof. Background technique [0002] Wheels are an important part of automobiles, and lightweight is the development trend of future automobiles. Forged aluminum alloy wheels have advantages in realizing automobile lightweighting, energy saving and emission reduction. Wheels are also the key parts and safety parts of the car. If the wheels are fatigued and cracked when the car is running at high speed, the car will be destroyed in light, and people will be killed in heavy. Therefore, while the wheels are lightweight, they also need to ensure sufficient mechanical properties and fatigue resistance. The existing forged aluminum alloy material, the fatigue performance can only cycle N=8x10 under the specified stress level σ=200Mpa 6 Left and right cycles, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/08C22C1/03C22F1/047C23C22/44B23P15/00B60C1/00
CPCC22C21/08C22C1/03C22C1/026C22F1/047C22F1/002C23C22/44B23P15/00B60C1/00Y02T10/86
Inventor 李洪光孙谱李庆丁有望李东东贾子瑞秦作峰穆瑞鹏
Owner 山东骏程金属科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More