Method for making brick with slag form smelting magnesium by Pidgeon process

A magnesium smelting and brick making machine technology, applied in the direction of sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problems of unutilized magnesium smelting slag and flue gas, environmental pollution, and atmospheric emissions. Achieve the effect of reducing cultivated land, reducing the amount of emissions, and reducing the impact of the greenhouse effect

Inactive Publication Date: 2003-03-12
朱广东
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] What the present invention aims to solve is the problem that the existing Pidgeon process metal magnesium smelting slag and flue gas are not utilized, and are directly discharged into the atmosphere, causing environmental pollution. Comprehensive utilization of preparation methods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] 1) Shovel out the magnesium smelting slag from the reducing tank, cool it naturally to normal temperature, then add 50% water to the magnesium smelting slag, and mix;

[0013] 2) Place the mixed slag at room temperature for one week;

[0014] 3) Send the mixed slag into the brick making machine for molding;

[0015] 4) The formed brick embryo is sent into the carbonization chamber, where it is carbonized by the carbon dioxide flue gas generated after the dolomite is calcined, and becomes a product.

Embodiment 2

[0017] 1) Shovel out the magnesium smelting slag from the reduction tank, cool it down to normal temperature naturally, then add 55% water to the magnesium smelting slag, and mix;

[0018] 2) Place the mixed slag at room temperature for one week, add 40% of the magnesium smelting slag and pulverize it into coal-fired cinders below 10mm, and mix evenly;

[0019] 3) Send the mixed slag into the brick making machine for molding;

[0020] 4) The formed brick embryo is sent into the carbonization chamber, where it is carbonized by the carbon dioxide flue gas generated after the dolomite is calcined, and becomes a product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A process for preparing Mg-slag brick includes collecting Mg slag from reducing reactor, natural cooling, mixing with water, still standing for 7 days, shaping, and carbnifying the brick blank by CO2 fume generated by calcining dolomite during smelting Mg. It can decrease environment pollution of smelting Mg.

Description

technical field [0001] The invention relates to a method for preparing bricks from Pidgeon process magnesium smelting slag. Background technique [0002] At present, most of the Pidgeon process magnesium smelting slag and flue gas are naturally discharged and buried, and a small part is sold by adding some cement to make blocks. pollute. Contents of the invention [0003] What the present invention aims to solve is the problem that the existing Pidgeon process metal magnesium smelting slag and flue gas are not utilized, and are directly discharged into the atmosphere, causing environmental pollution. Comprehensive utilization of the preparation method. [0004] Technical solution of the present invention is realized like this. A method for preparing bricks from Pidgeon process magnesium smelting slag, the steps of the preparation method are: [0005] 1) Shovel out the magnesium smelting slag from the reducing tank, cool it naturally to normal temperature, then add 50-6...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B18/14C04B30/00C04B41/50
CPCC04B30/00C04B41/009C04B18/144C04B41/85C04B41/50Y02W30/91C04B41/4529C04B41/4556C04B18/067
Inventor 朱广东
Owner 朱广东
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap