Zinc-particle processing method for making electrogalvanizing steel plate

A processing method, electrogalvanizing technology, applied in the field of metal particle processing, can solve the problems of finished zinc particle pollution, low labor productivity, large maintenance, etc., and achieve the effects of reduced processing cost, high processing efficiency, and low processing energy consumption

Inactive Publication Date: 2003-08-27
上海宝鹏有色金属制品厂
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the main problems are: ①The process is complex and there are many processing procedures; ②The recovery rate of zinc particles is low, less than 70%; ③The energy consumption is high, and more than 30% of the leftover materials need to be returned to remelt, which consumes more than 30% more energy; ④ Huge stamping equipment, heavy maintenance and low labor productivity; ⑤ High investment in equipment construction; ⑥ Pollution to finished zinc particles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zinc-particle processing method for making electrogalvanizing steel plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] First put the zinc ingot 1 in the melting furnace 2, the melting furnace is a 50kw resistance furnace, after the molten zinc is melted, because its density is lower than that of the zinc ingot, the molten zinc floats up, and the molten zinc flows out of the melting furnace from the liquid outlet 3, and the liquid is discharged The height from the mouth to the liquid level is 55mm. The zinc liquid flows into the holding furnace 5 through the graphite tube 4 with a diameter of φ18mm. The holding furnace adopts a ceramic inner heating sleeve 6 for heating, and the temperature of the zinc liquid 7 is controlled at 436-440°C. 2 Protection against surface oxidation of zinc liquid. The through hole 8 in the lower part of the holding furnace is connected with the metering device 9, and the zinc liquid flows into the metering device through the through hole, and directly drips onto the graphite cooling roller 11 after passing through the drip nozzle 10, and the dripping distance...

Embodiment 2

[0044] First, place the zinc ingot 1 in the melting furnace 2. The melting furnace is a 46kw resistance furnace. After the molten zinc is melted, because its density is lower than that of the zinc ingot, the molten zinc floats up, and the molten zinc flows out of the melting furnace from the liquid outlet 3. The height to the liquid surface is 62mm. The zinc liquid flows into the holding furnace 5 through the ceramic tube 4 with a diameter of φ12mm. The holding furnace adopts a ceramic inner heating sleeve 6 for heating, and the temperature of the zinc liquid 7 is controlled at 437-442°C. 2 Protection to prevent oxidation of the zinc liquid surface. The through hole 8 in the lower part of the holding furnace is connected with the metering device 9. The zinc liquid flows into the metering device through the through hole, and directly drops onto the graphite cooling roller 11 after passing through the drip nozzle 10. The dripping distance from the drip nozzle outlet to the cooli...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The production method of zinc granules for making galvanized sheet steel includes: melting zinc pig in melting furnace, feeding the melton zinc into heat-insulating furnace, said heat-insulating furnace adopts heating sleeve in the ceramic to supply heat, when the molten zinc is heat-insulated, the N2 or Ar2 can be used for protection. The temp. of molten zinc in the heat-insulating furnace is controlled in 435-455 deg.C. The lower portion of heat-insulating furnace is equipped with one or more than one through hole. Said through hole is directly connected with batchmeter, the molten zinc is flowed through the batchmeter and drip nozzle, then dripped on the gypsum cooling roller whose rotating speed is 30 rmp-80 rpm, 50%-80% of roller body area of cooling roller can be soaked in the condensated water tank whose internal water temp. is 15 deg.C-45 deg.C, so that the molten zinc can be quickly changed into zinc granules.

Description

1. Technical field [0001] The invention belongs to the technical field of metal particle processing, and relates to a method for processing metal particles, in particular to a method for processing zinc particles for manufacturing electrogalvanized steel sheets. 2. Background technology [0002] The development of the automobile industry puts forward higher requirements on the strength and corrosion resistance of steel plates. In order to meet the needs of the automobile industry, high-strength electro-galvanized steel sheets are developing rapidly. When manufacturing electro-galvanized steel sheets, electroplating is a key process. When electroplating steel sheets, zinc ions in the plating solution are mainly supplemented by adding zinc ingots or zinc particles, which are then dissolved in the plating solution. The method of supplementing zinc ions by adding zinc ingots in the plating solution has the disadvantages of inconvenient operation and uneven composition of the pla...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F9/08B22F9/10
Inventor 陆汉锷陈群周德忠余益祥
Owner 上海宝鹏有色金属制品厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com