High strength steel fibre concrete and making method thereof

A high-strength concrete and steel fiber technology, applied in the field of concrete, can solve the problems of high compressive strength, poor toughness, and poor frost resistance, and achieve the effects of high compressive strength, large bearing capacity, and good frost resistance.

Inactive Publication Date: 2003-10-29
杨果林 +1
View PDF0 Cites 47 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Cement concrete products generally have high compressive strength, but have low flexural and tensile strength, poor toughness, and poor frost resistance (not suitable for construction in winter). increases, the production process becomes complex

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0008] The following are non-limiting examples of the invention:

[0009] Used to make steel fiber high-strength concrete manhole covers

[0010] Concrete formula (percentage by weight): 20% cement, 3.5% fly ash, 4.5% silica fume, 5% water, 2.5% steel fiber, 23% sand, 34.3% crushed stone, 0.25% water reducer, cold rolled ribbed Rebar 7%.

[0011] Production method: 1. Preparation of raw materials and mold preparation of the cover plate and cover seat of the manhole cover, and distributing steel bars in the mold of the cover plate and cover seat. 2. Raw materials are mixed according to the specified ratio. 3. The cement , fly ash, and silica fume are poured into the mixer and mixed for 2-3 minutes. 4. Then, the coarse and fine aggregate gravel and sand are poured into the mixer and mixed for 2-3 minutes. 5. The water reducer is dissolved in water 6. Pour the water dissolved in the water reducer into the mixer for wet mixing for 3-5 minutes. 7. Disperse the steel fibers in the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A steel fibre reinforced high-strength concrete is prepared from cement, flyash, silicon ash, water, steel fibres, sand, broken stone and water-reducing agent through providing raw materials and mould, sequentially and proportionally mixing, stirring, pouring in mould, vibration, natural curing, demoulding, standard curing and inspection.

Description

technical field [0001] The invention belongs to the technical field of concrete, and relates to a steel fiber high-strength concrete and a manufacturing method thereof. Background technique [0002] Cement concrete is the main building material in buildings. It is generally made of cement, sand, gravel, and water. After mixing evenly, it is formed and solidified. Cement concrete products generally have high compressive strength, but have low flexural and tensile strength, poor toughness, and poor frost resistance (not suitable for construction in winter). increase, the production process becomes complicated. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a steel fiber high-strength concrete and a manufacturing method thereof aiming at the shortcomings of existing concrete. [0004] The technical solution adopted to solve the technical problem of the present invention is that the steel fiber high-strength concr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B14/02C04B14/48C04B18/08C04B28/04
CPCY02W30/91
Inventor 杨果林林小松
Owner 杨果林
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com