Fire resistant sheet substrate material like leather and producing method thereof

A flame-retardant, sheet-like technology, applied in the direction of flame-retardant fibers, chemical instruments and methods, non-woven fabrics, etc.

Inactive Publication Date: 2004-01-21
KURARAY CO LTD
View PDF7 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these patent documents do not disclose the use of the flame-retardant polyester fiber or flame-retardant polyurethane to manufacture flame-retardant similar leather sheet-like substrates. Moreover, the surface strength such as abrasion resistance or peel strength is good, and the flame retardancy is similar to leather sheet substrates. These patent documents do not have any hint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

manufacture example 1～4

[0148] "Manufacturing Examples 1-4" [Manufacture of polyester, spinning and manufacture of staple fiber]

[0149] (1) In terephthalic acid and ethylene glycol, 0.04 mass % of titanium dioxide is added based on the mass of terephthalic acid, and antimony trioxide is added in a ratio of 500 ppm based on the mass of terephthalic acid. Heating is carried out under the condition of 2.0 Pa, the esterification reaction is carried out until the esterification rate is more than 95%, and the oligomer is produced. Add the oligomer and reactive phosphorus flame retardant (M-Ester manufactured by Sanko Co., Ltd., molecular weight 434, phosphorus atom content 7% by mass) according to the ratio shown in Table 1 below. , Under a reduced pressure of 40.0 Pa, it is melt-polymerized to generate a prepolymer with an intrinsic viscosity of 0.65 dl / g, and the prepolymer is extruded into strips through a nozzle, and cut into small cylindrical pieces. After pre-drying the pellet at 120°C for 2 hours...

Embodiment 1

[0153] "Example 1" [manufacture of flame-retardant similar leather sheet substrate and imitation suede artificial leather]

[0154] (1) Use the staple fiber of the island-in-sea type composite spun fiber using the polyester that does not contain phosphorus atoms obtained in Manufacture Example 1, and adopt the ring weaving method to manufacture the unit area weight 130g / m according to the usual method 2 fabric.

[0155] (2) Using the phosphorus copolyester obtained in Manufacturing Example 3 as the staple fiber of the sea-island type composite spun fiber of the island component, the weight per unit area 520g / m is produced according to the usual method by the circular weaving method 2 fabric.

[0156] (3) Composite the fabric produced by the above (1) with the fabric produced by the above (2) to form a weight per unit area of ​​650g / m 2 After the composite fabric, a total of about 2500p / cm is carried out alternately from both sides 2 of acupuncture. Then, after shrinking tr...

Embodiment 2

[0168] "Example 2" [manufacture of flame-retardant similar leather sheet substrate and imitation suede artificial leather]

[0169] (1) Using the short fiber of the sea-island type composite spun fiber that does not contain the phosphorus atom obtained in Production Example 1 as the island component, the basis weight of 390 g / m was produced in the same manner as in Example 1 (1). 2 fabric.

[0170] (2) Using the phosphorus copolyester obtained in Manufacturing Example 4 as the staple fiber of the sea-island type composite spun fiber of the island component, a weight per unit area of ​​260 g / m was produced in the same manner as in Example 1 (2). 2 fabric.

[0171] (3) After the operation of compounding the fabric produced by the above (1) and the fabric produced by the above (2), carry out the same operation as in Example 1 to produce a smooth entangled nonwoven fabric (weight per unit area: 1,050 g / m 2 , the apparent density is 0.45g / cm 3 ).

[0172] (4) Using the entangle...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The flame-retardant leather-like sheet substrate of the present invention comprises a layer (A) that is made of an entangled nonwoven fabric comprising a polyester superfine fiber (a) of a single fiber fineness of 0.5 dtex or less containing no flame-retardant component and a flame-retardant polyester superfine fiber (b) of a single fiber fineness of 0.5 dtex or less containing a flame-retardant component in a ratio, (a) / (b), of 100 / 0 to 40 / 60 by mass, and a layer (B) that is made of an entangled nonwoven fabric comprising the polyester superfine fiber (a) and the flame-retardant polyester superfine fiber (b) in a ratio, (a) / (b), of 70 / 30 to 0 / 100 by mass. The entangled nonwoven fabrics of the layers (A) and (B) are impregnated with an elastomeric polymer (c) containing a flame-retardant component. The ratio of the polyester superfine fiber (a) and the flame-retardant polyester superfine fiber (b) in the flame-retardant leather-like sheet substrate is 10:90 to 90:10 by mass. The flame-retardant leather-like sheet substrate and the artificial leather made thereof have an excellent flame retardancy, a soft and high-quality feeling and appearance, a high abrasion resistance and peel strength, and excellent mechanical properties such as surface strength.

Description

technical field [0001] The present invention relates to a flame-retardant leather-like sheet-like substrate and a manufacturing method thereof, an artificial leather using the flame-retardant leather-like sheet-like substrate, and a chair or vehicle seat using the artificial leather as a surface layer. More specifically, the present invention relates to a flame-retardant leather-like sheet-like base material having a soft and high-quality feel, good surface strength such as abrasion resistance or peel strength, and a method for producing the same, and the use of the flame-retardant material. Artificial leather with properties similar to a leather sheet substrate. The flame-retardant leather-like sheet-like base material of the present invention and the artificial leather using the base material are suitable for making use of the above-mentioned characteristics, having a high-end feel, and requiring high surface strength such as flame retardancy and high abrasion resistance or ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B5/26B32B27/36D04H13/00D06M11/45D06M13/282D06N3/00
CPCY10S428/904B32B5/26D06M2200/30D06N3/0063D06N3/0013D06M11/45D06M13/282B32B27/36D04H13/006D04H1/435D04H1/46D04H1/482D04H1/488D04H1/492D04H1/498Y10T442/2631Y10T442/659D06N3/04B32B2262/0276B32B5/022
Inventor 延藤芳树安田佳明丹波善博
Owner KURARAY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap