A sealant, road technology, used in adhesives, adhesive types, other chemical processes, etc., to achieve strong adhesion, high temperature stability, and good resilience

Inactive Publication Date: 2005-03-23
SENYUAN CHEM IND ANSHAN
View PDF0 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In view of the above problems, the present invention provides a new formula technology, the purpose of which is to overcome the shortage of asphalt used for road surface crack sealing, and provide a high-performance road crack sealant, which will not soften and deform at high temperature, and will not be damaged. The wheel is taken away, it has high elasticity at low temperature and does not crack, and can elastically deform with the expansion and contraction of cracks, with strong adhesion, and always seals cracks on the road surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Petroleum pitch: 100 parts

[0022] SBS: Linear: 8 parts

[0023] Star shape: 2 servings

[0024] Aliphatic petroleum resin: 4 parts

[0025] Aromatic petroleum resin: 2 parts

[0026] Polyisobutylene: 0.5 parts

[0027] T501: 0.3 parts

[0028] Butadiene rubber: 0 parts

[0029] Stabilizer: 0.25 parts

[0030] Paraffin oil: 8 parts

[0031] Rubber powder: 8 parts

[0032] Anti-stripping agent: 0.5 parts

[0033] Talc powder: 30 parts

[0034] Limestone powder: 15 parts

[0035] The performance indicators of the sealant prepared by the above formula are: softening point 93°C, melt viscosity: 2600mPa·S, penetration (1 / 10mm) at 25°C: 66, elastic recovery at 25°C: 98.6%, ductility at 25°C (cm): 53.

Embodiment 2

[0037] Petroleum pitch: 100 parts

[0038] SBS: Linear: 7 copies

[0039] Star shape: 2 servings

[0040] Aliphatic petroleum resin: 5 parts

[0041] Aromatic petroleum resin: 2 parts

[0042] Polyisobutylene: 0.5 parts

[0043] T501: 0.3 parts

[0044] Butadiene rubber: 4 parts

[0045] Stabilizer: 0.25 parts

[0046] Paraffin oil: 11 parts

[0047] Rubber powder: 5 parts

[0048] Anti-stripping agent: 0.5 parts

[0049] Calcium Carbonate: 38 parts

[0050] The performance indicators of the sealant prepared by the above formula are: softening point 90.5°C, melt viscosity: 3100mPa·S, penetration (1 / 10mm) at 25°C: 89, elastic recovery at 25°C: 99%, ductility at 25°C (cm): 51.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Softening pointaaaaaaaaaa
Melt viscosityaaaaaaaaaa
Extensibilityaaaaaaaaaa
Login to View More

Abstract

The invention is a sealant special for sealing cracks of bituminous pavement, it contains (in weight share): petroleum pitch 100 shares, SBS 9-15 shares, tackifying resin 4-10 shares, antiageing agent 0.2-1 share, synthetic rubber 0-4 shares, stabilizer 0.15-0.45 share, softening agent 2-16 shares, viscosity-regulator 2-15 shares, antistripping agent 0.2-0.5 share, and reinforcing agent 35-60 shares. It has weak temperature sensitivity, strong adhesion and good elasticity.

Description

technical field [0001] The invention relates to a road crack sealant which is specially used for crack filling and sealing of asphalt pavement cracks. Background technique [0002] The traditional filling and sealing of pavement cracks is to pour ordinary petroleum asphalt into the cracks by heating and melting. Due to the strong temperature sensitivity of asphalt, it becomes soft and flowing in summer, and is carried away by the wheels, and becomes hard and brittle in winter, loses elasticity, and cracks. It is very uneconomical to refill the joints in the second year. [0003] In view of the above problems, the present invention provides a new formula technology, the purpose of which is to overcome the shortage of asphalt used for road surface crack sealing, and provide a high-performance road crack sealant, which will not soften and deform at high temperature, and will not be damaged. The wheel is taken away, it has high elasticity and does not crack at low temperature, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J195/00C09K3/10E04B1/68
Inventor 张敏刘春晓
Owner SENYUAN CHEM IND ANSHAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com