Metal laser deep-layer quenching process

A laser and metal technology, applied in the field of metal laser deep quenching process, can solve the problems of shallow depth of laser quenching and hardening, etc.

A laser and metal technology, applied in the field of metal laser deep quenching process, can solve the problems of shallow depth of laser quenching and hardening, etc.

CN1603425AInactive Publication Date: 2005-04-06ZHEJIANG UNIV OF TECH
0 Cites 16 Cited by

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal laser deep-layer quenching process
  • Metal laser deep-layer quenching process
  • Metal laser deep-layer quenching process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] Combine below figure 1 , figure 2 and image 3 A detailed description of the embodiment of the present invention, the laser spot can be a rectangular laser spot, or a circular spot such as figure 1 , 1 is the laser beam, the size of the spot can be adjusted, the flow and direction of the coolant 2 are fixed, the injection direction of the coolant 2 is 5-15° to the outside, and the distance from the spot can be adjusted, during the process of the coolant 2, The gas 3 and the laser beam 1 move synchronously. The gas 3 is argon, which not only has a cooling effect, but also has a protective effect on the laser active area. Take woodworking knives as an example, such as figure 2 , image 3 As shown, the knife is made up of a knife body 5 and a blade 4. Originally, the blade 4 was manufactured by brazing and inserting high-speed steel or hard alloy. The main problem is that the process is complicated. For the hard alloy edge, due to the brittleness of the material its...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
depthaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

One kind of metal laser deep layer quenching craft, through must process the area surface spreading alloy extinction coating after the metal, according to processes the area choice certain facula the light beam to carry on laser processing, simultaneously, blows the metal surface laser partial with the certain current capacity gas sphere of action, and with the liquid cooling laser sphere of action periphery, causes the metal hardening level quenching depth to achieve 0.7~~3mm. The invention has solved the metal induction heating time deformation, enhanced the metal skin hardness, simultaneously has solved an ordinary laser quenching hardening depth shallower problem.

Description

technical field [0001] A metal laser deep quenching process, suitable for surface quenching and hardening of metal materials, especially for parts with complex shapes and parts that do not allow deformation, such as the surface layer of large and medium-sized gears, the inner and outer rings of large bearings, and the processing of tool blades, etc. . Background technique [0002] The current metal processing usually adopts the method of induction heating and quenching to improve the surface hardness of the metal. Although the depth is relatively deep, it can reach 1-3mm, but the surface will melt during heating, which not only destroys the metal surface finish, but also deforms the workpiece greatly. The production of the induction coil is complicated, especially the part of the inner cavity of the workpiece with complex shapes, which is difficult to harden. [0003] Laser hardening metal processing technology is also widely used at home and abroa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
06 Apr 2005
Publication
CN1603425A
IPC
C21D1/09
Inventors
姚建华; 楼程华