Production for ceramic composite bricks

A manufacturing method and composite brick technology, which is applied in the field of ceramic brick production, can solve the problems of high production cost, non-wear-resistant finished product surface, high brick damage rate, etc., and achieve the effect of bright colors, good surface quality and high mechanical strength

Inactive Publication Date: 2005-05-11
FOSHAN SHI WAN YING BRAND CERAMICS CO LTD
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The manufacture of composite bricks in the prior art generally adopts the method of two moldings, that is: firstly mix the ingredients, melt them into frits at 1380-1400°C, make the fineness below 5 mesh, and directly mix the above-mentioned various frits Prepare the ceramic body, and press the ceramic brick powder into shape; then sprinkle the above-mentioned mixed frit mixture on the ceramic brick, apply a fixative to fix it, and finally fire it; the disadvantage of the above-mentioned manufacturing method is that Two-time molding is adopted, the brick damage rate is high, and the firing is complicated, the yield is low, the surface of the finished product is not wear-resistant, and the production cost remains high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Use feldspar, sand, clay, limestone, talc, wollastonite, zircon sand and other ceramic raw materials in the usual way to prepare powder ① according to a certain formula ratio, ball milling, and granulation; take powder ① and put it in the factory The 60# frit used is mixed according to a certain formula ratio to obtain powder ②; on the basis of the formula of powder ②, 0.1-0.2% Paris red material is added, and ingredients, ball milling, and granulation are carried out according to the usual method to obtain Powder ③; on the basis of the formula of powder ②, add 0.5-0.6% titanium dioxide and 0.1-0.2% orange-yellow material, and carry out batching, ball milling, and granulation according to the usual method to obtain powder ④; according to the conventional method Grind the powder ① into fine powder a, grind the powder ③ into fine powder b, grind the powder ④ into fine powder c, mix according to the ratio of fine powder a: fine powder b: fine powder c = 5:2:3, mix slightly,...

Embodiment 2

[0025] Prepare powder ①, powder ③, powder ④ by the method of example 1. Take the powder ① and the 30# frit used in the factory, and mix, ball mill, and granulate according to a certain formula ratio to obtain the powder ⑤. Using the powder ④ as the base material, the powder ③ and the powder ⑤ as the flower material, according to the production method of the multi-tube cloth porcelain tile, press it into a brick, and after firing and polishing, the surface has a transparent and three-dimensional color spot. .

Embodiment 3

[0027] Prepare powder ① and powder ② according to the method of Example 1, add 0.1-0.2% Paris red material on the basis of the formula of powder ②, and carry out batching, ball milling, and granulation according to the usual method to obtain 2-8 mesh particles a. According to the proportion of powder ①:a=90:10, mix evenly to obtain powder ⑥. According to the conventional method of producing porcelain tiles, the first distribution is to fill the powder ① in the lower mold, and then the second distribution is to fill the powder ⑥ on the powder ①. The upper mold of the mold is smooth. The polished tiles are obtained by forming, firing and polishing according to the usual method, and the polished tiles present transparent, three-dimensional texture and irregularly distributed red particles.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Production for composite ceramic tiles is carried out by: 1) preparing powder of ceramic tile; 2) mixing the powder with frit by proportion of powder : frit=(4-6) : (6-4) to obtain batching raw material, adding pigment or toner, ball milling, granulating to obtain the raw material powders; 3) mixing one or several raw material powder with powder of ceramic tile to obtain mixed powder; 4) mixing the mixed powder with the powder of ceramic tile; and 5) pressing forming the mixed powder, baking in furnace and surface treating the base tile. It achieves simple process and high quality.

Description

technical field [0001] The invention relates to the technical field of ceramic tile production, in particular to a method for manufacturing porcelain composite tiles with glass-ceramic surfaces and transparent, translucent and colorful three-dimensional texture effects. Background technique [0002] The manufacture of composite bricks in the prior art generally adopts the method of two moldings, that is: firstly mix the ingredients, melt them into frits at 1380-1400°C, make the fineness below 5 mesh, and directly mix the above-mentioned various frits Prepare the ceramic body, and press the ceramic brick powder into shape; then sprinkle the above-mentioned mixed frit mixture on the ceramic brick, apply a fixative to fix it, and finally fire it; the disadvantage of the above-mentioned manufacturing method is that Adopt twice forming, the damage rate of adobe is high, and the burning is complicated, the finished product rate is low, the surface of the finished product is not we...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/02C04B33/13C04B35/14C04B35/622
Inventor 钟应洲林伟何伟杰吴俊峰
Owner FOSHAN SHI WAN YING BRAND CERAMICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com