Metal surface lacquer with flip-flop effect and its preparing method

A technology of changing color with angle and metal surface, which is applied in the field of metal topcoat with effect of changing color with angle and its preparation, and achieves the effect of enhancing anti-ultraviolet ability, improving weather resistance and good stability

Inactive Publication Date: 2005-08-03
FUDAN UNIV
View PDF2 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no metal flash automotive topcoat technology and related patent reports modified by inorganic nanoparticles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal surface lacquer with flip-flop effect and its preparing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Formula 1 for metallic finishes with flop effects

[0046] Ingredient parts by weight wt(%)

[0047] Nano particle dispersion 4.8

[0048] Setal173 (polyester resin) 21

[0049] Setamine138 (amino resin) 5.5

[0050] BI7982 (modified resin) 3.7

[0051] Metallux2154 (aluminum powder) 3.5

[0052] CAB381-0.5 (aluminum powder directional agent) 4.7

[0053] Solvent 56

[0054] Auxiliary 0.8

[0055] The above formula is prepared according to the preparation method proposed by the invention, and a metal topcoat with a color-dependent effect can be obtained. The color-dependent effect of the coating (visual inspection): good, stone chip resistance: ≤2 grades, gloss (Gloss 20°) 97, Haze Hlog 95, artificial accelerated aging resistance time ≥ 1500 hours, other coating properties passed GB / T13492-92.

Embodiment 2

[0057] Metallic topcoat formulation with floppy effect 2

[0058] Ingredient parts by weight wt(%)

[0059] Nanoparticle dispersion paste 7.4

[0060] Desmophen 650 (polyester resin) 37

[0061] Setamine133 (amino resin) 21.3

[0062] Metallux2154 (aluminum powder) 1.3

[0063] CAB381-0.5 (aluminum powder directional agent) 3.3

[0064] Solvent 30.6

[0065] Auxiliary 1.1

[0066] The above formula is prepared according to the preparation method proposed by the invention, and a metal topcoat with a color-dependent effect can be obtained. The color-dependent effect of the coating (visual inspection): good, stone chip resistance: ≤2 grades, gloss (Gloss 20°) 95, haze (Haze Hlog) 127, artificial accelerated aging resistance time ≥ 1500 hours, good wear resistance of the coating, other coating properties passed GB / T13492-92.

Embodiment 3

[0068] Metallic topcoat formulation with floppy effect 3

[0069] Ingredient parts by weight wt(%)

[0070] Nano particle dispersion slurry 0.9

[0071] Desmophen 650 (polyester resin) 14

[0072] Setal173 (polyester resin) 12

[0073] Setamine133 (amino resin) 7.1

[0074] C1158 (amino resin) 2.6

[0075] Vestanat BI358A (modified resin) 6.9

[0076] SSP504-AR (aluminum powder) 7.7

[0077] CAB381-0.5 (aluminum powder directional agent) 2.5

[0078] CAB551-0.2 (aluminum powder directional agent) 4

[0079] Pearlescent Pigment 3

[0080] Solvent 36.9

[0081] Auxiliary 2.4

[0082] The above formula is prepared according to the preparation method proposed by the invention, and a metal topcoat with a color-dependent effect can be obtained. The color-dependent effect of the coating (visual inspection...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a kind of metal surface lacquer with flip-flop effect and its preparation process. The metal surface lacquer with flip-flop effect is prepared with dispersive nanometer particle slurry with flip-flop effect together with polyester resin, amino resin, closed isocyanate modified resin, metal aluminum powder, pigment and stuffing, solvent and assistant, and through certain technological process. The present invention has nanometer particle dispersed homogeneously in paint, and the prepared metal surface lacquer has high brightness, low haze value, obvious flip-flop effect, excellent decoration effect, high scrape resistance, high stone attack resistance, high wear resistance and good ageing resistance. The lacquer is used for car surface, outer metal decoration, etc.

Description

technical field [0001] The invention belongs to the field of chemical industry, and relates to a metal topcoat with an angle-dependent color effect and a preparation method thereof. Background of the invention [0002] The high-grade and high-performance requirements of automobiles force the development of automobile coatings to continuously improve their protection and decoration performance. The main focus is to improve the decoration of the car surface, improve the scratch resistance and anti-corrosion ability, and better protect the environment, especially the surface protection and decoration layer of the car body, which directly affects the appearance and appreciation of the whole car. [0003] The research and development and industrialization of nano-materials for modified automotive coatings started earlier in the United States and Germany, and the research and development of nano-modified automotive coatings started relatively late in China. CN1189522A, a patent fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B05D7/14C09D167/00
Inventor 武利民刘娅莉于占锋游波周树学
Owner FUDAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com