Positive pole materical for alkaline secondary battery and alkaline secondary battery
A cathode material, secondary battery technology, applied in alkaline batteries, battery electrodes, nickel batteries, etc., can solve problems such as poor self-discharge performance, and achieve the effects of improving self-discharge performance, delaying dissolution, and improving self-discharge performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0028] Example 1
[0029] This example illustrates the positive electrode material provided by the present invention, the alkaline secondary battery containing the positive electrode material and their preparation methods.
[0030] (1) Preparation of positive electrode
[0031] 100 parts by weight of spherical nickel hydroxide, 5 parts by weight of cobalt oxide, 0.5 parts by weight of metal tungsten powder, and 5 parts by weight of carboxymethyl cellulose aqueous dispersion (containing 1% by weight of carboxymethyl cellulose) , 2 parts by weight of polytetrafluoroethylene (PTFE) dispersion (a standard product with a solid content of 60% by weight), 20 parts by weight of water are mixed and stirred to form a paste slurry, and the slurry is filled with a surface density of 430 g / m2, in the nickel foam with a nickel strip drain terminal welded on one side, and then dried, rolled, and cut to obtain a positive electrode plate with a size of 85 mm × 40 mm × 0.65 mm, in which the hydroxi...
Example Embodiment
[0039] Example 2
[0040] This example illustrates the positive electrode material provided by the present invention, the alkaline secondary battery containing the positive electrode material and the preparation method thereof.
[0041] The battery cathode material and battery were prepared according to the method of Example 1, respectively, except that when preparing the cathode, the amount of metal tungsten powder added was 1 part by weight, and the amount of cobalt oxide added was 2.5 parts by weight to form battery B2.
Example Embodiment
[0042] Example 3
[0043] This example illustrates the positive electrode material provided by the present invention, the alkaline secondary battery containing the positive electrode material and the preparation method thereof.
[0044] The battery cathode material and battery were prepared according to the method of Example 1 respectively. The difference is that when preparing the cathode, the amount of metal tungsten powder added in Example 3 was 2 parts by weight, and cobalt metal powder and cobalt trioxide were used instead of cobalt oxide. Based on the cobalt element, the amounts of cobalt metal powder and cobalt trioxide are 4 parts by weight and 3 parts by weight to form battery B3.
[0045] The following describes the performance of the battery provided by the present invention.
[0046] (1) The batteries B1-B3 made in Examples 1-3 and Comparative Example BB1 were charged at 210mA (0.1C) for 15 hours, left for 30 minutes, and discharged at 630mA (0.3C) to 1.0V.
[0047] ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap