Method for making fluxed iron ore powder composite pellet

A production method and technology of composite pellets are applied in the field of production of flux-based iron ore powder composite pellets, which can solve problems such as unformed production processes, and achieve the effects of being beneficial to increasing blast furnace production, saving energy consumption and reducing investment.

Inactive Publication Date: 2006-07-19
许贵宾
View PDF0 Cites 44 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this flux-based pellet has no finalized production process so far.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for making fluxed iron ore powder composite pellet
  • Method for making fluxed iron ore powder composite pellet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0049] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below in conjunction with the accompanying drawings.

[0050] The invention relates to a production method of flux-based iron ore powder composite pellets, which adopts multiple pelletizing methods to produce single-ball double-alkalinity composite flux-based pellets, that is, in the first pelletizing process, according to the production Required binary alkalinity (CaO / SiO 2 ) requirements, so that the green balls contain an appropriate amount of CaO and MgO, and then carry out the second ball making, and evenly coat the outer layer of the green ball surface with limestone powder, dolomite powder, hematite dry powder or low-Si acidic iron concentrate powder Anti-adhesion layer, etc., and then use the baking temperature and baking method of the acidic pellets to bake to ensure that the pellets do not bond.

[0051] Th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The preparation method for a solvent-type iron ore composite aggregate comprises: ensuring the proper CaO and 2-4% MgO with weight o.5-2.0 in the first process; then coming the secondary time, wrapping one block layer evenly of CaCo3 powder, dolomite powder, hematite dried powder or acidic iron concentrate ore; then, baking as the acidic aggregate baking temperature and means to ensure the ore not bond. This invention overcomes bonding problem with low cost and little pollution, and improves blast furnace yield even meets the pH balance or desulfurization request.

Description

technical field [0001] The present invention relates to a production method of flux-based iron ore powder composite pellets, more precisely, relates to a flux-based iron ore powder composite ball that can better solve the bonding problem of flux-based pellets in the roasting process The invention discloses a method for producing dough; it belongs to the technical field of charge preparation in the ironmaking process. Background technique [0002] At present, the production technology of ironmaking furnace materials in my country is not optimistic. The ironmaking raw materials of various iron and steel plants are basically high-basic sinter with a small amount of acid pellets. Taking 2003 as an example, sintered ore accounted for more than 80%, and pellet ore accounted for only about 12%. The proportion of pellets in most steel plants has not exceeded 30%. Compared with sinter, pellets have many advantages such as high grade, uniform particle size, high strength, less powde...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22B1/14
Inventor 许贵宾
Owner 许贵宾
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com