Photocurable resin composition, and its preparing method and use

A compound and light-curing technology, applied in the field of materials, can solve problems such as insufficient curing degree and short curing time

Active Publication Date: 2011-04-20
SHANGHAI SHOWA HIGHPOLYMER CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This technology can use all light from visible light to near-infrared for curing operations, which is safe and has a short curing time. It effectively solves the problems caused by peroxide curing, but it does not fundamentally solve the surface layer that is in contact with the air during curing. Part of the problem of insufficient curing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Photocurable resin composition, and its preparing method and use
  • Photocurable resin composition, and its preparing method and use
  • Photocurable resin composition, and its preparing method and use

Examples

Experimental program
Comparison scheme
Effect test

application example 1

[0096] To 100 parts of vinyl ester resin [VE-1], add 1.5 parts of a diacylphosphine oxide compound photoinitiator that is photosensitive to all light in the wavelength range from ultraviolet light to visible light: two (2, 4, 6- Trimethylbenzoyl)-phenylphosphine oxide (trade name: Irgacure 819, produced by Ciba Seika Co., Ltd., hereinafter referred to as I-819), obtained a photocurable resin composition-1 capable of photosensitivity to all light in the wavelength range from ultraviolet light to visible light. The composition contains Hydroxyl amine compounds.

[0097] Then pour the photocurable resin composition into a frame made of glass plate to a thickness of 3 mm, and then use a 2KW metal halide lamp [trade name: Dynabeam2, manufactured by Toshiba Lighting Technology Co., Ltd.], which is a visible light source. Irradiate it at a distance of 1m for ten minutes to fully cure it. The bending strength and Barcol hardness (BH) of the obtained molded panels were measured. Th...

comparative example 1

[0099] A room temperature curing catalyst butanone peroxide / cobalt naphthenate (Co: 6%)=1.0 part / 0.5 part was added to 100 parts of vinyl ester resin [VE-1] to obtain room temperature curable resin composition-1.

[0100] Then, the room temperature curable resin composition-1 was poured into a frame made of glass plate so that the thickness reached 3 mm, and it was left at room temperature for 24 hours to be cured at room temperature. Then prepare a molded plate that has undergone secondary post-curing for two hours at 120° C., and measure the flexural strength and Barcol hardness (BH) of the molded plate. The results are shown in Table 1. It can be seen from Table 1 that when the room temperature curable resin composition-1 is cured at room temperature, the same hardness as room temperature curing + secondary post-curing cannot be obtained even after curing for 24 hours. Resin composition-1 can obtain hardness and physical properties equivalent to room temperature curing + s...

application example 2

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

Composition of the visible light solidified resin includes following portions in wt%: (1) 100 portions of collective compound containing at least one unsaturation group in olefin class (such as unsaturated polyester, vinyl ester etc.); (2) 10-100 portions of at least one monomer containing unsaturation group in olefin class; (3) adding 0.05-5 portions of photoinitiator in free radical type to 100portions of resin; (4) adding 0.1- 1000ppm portions of metal salt to 100 portions of resin; (5) adding 0.1- 10 portions of amine compound to 100 portions of resin. Using visible light solidifies the resin. Other reinforcing material can be added to meet different methods to produce products of glass fiber reinforced plastic. Solving issues of solidified peroxide and not good operability, the invention also solves issue, which is not solved by other visible light solidifying methods, of not enough solidifying surface layer contacted to air.

Description

technical field [0001] The present invention relates to the field of materials, in particular to a resin composition, in particular to a photocurable resin composition and its preparation method and application. Background technique [0002] The cured resin composition of the present invention can be widely used in the fields of corrosion-resistant FRP lining, FRP molding, casting, coating, primer, putty, etc., and has rapid curing, low-temperature curing and excellent physical properties. [0003] In the fields of FRP molding, FRP lining, casting, coating, primer, putty, etc., unsaturated polyester resin, vinyl ester resin, polyurethane acrylate resin, polyurethane methacrylate resin, polyacrylate resin, Polymethacrylate resin, polyether acrylate resin, polyether methacrylate resin, epoxy resin, phenolic resin and other thermosetting resins, unsaturated polyester resin, vinyl ester resin, polyurethane acrylate resin in these resins , Urethane methacrylate resin, polyacryla...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G03F7/004G03F7/027G03F7/028
Inventor 大谷和男江先龙
Owner SHANGHAI SHOWA HIGHPOLYMER CO LTD