Thin layer multi coloured sand wall shaped paint

A color paint and coating technology, applied in the direction of coating, can solve the problems of limited color, weak covering power and high cost, and achieve the effect of reducing the amount of paint, full color, and improving crack resistance.

Inactive Publication Date: 2007-01-31
巢启
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a thin-layer multi-color sand wall paint with the color characteristics of latex paint, so as to overcome the shortcomings of the currently used sand wall paint that the color is limited to stone color, weak hiding power, large dosage and high cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Raw material formula:

[0028] Acrylic emulsion 15 kg Titanium white paste 7 kg

[0029] Polyvinyl alcohol hydrosol 2 kg Hydroxyethyl cellulose hydrosol 20 kg

[0030] Alcohol Ester-12 0.5 kg SN5040 0.5 kg

[0031] NXZ 0.1 kg Huake-981 1.5 kg

[0032] Thickener-1306 and HAS663 0.15 kg 120-200 mesh stone powder of various colors 25 kg

[0033] 100-150 mesh color coating film 0.5 kg 200-300 mesh stone powder of various colors 20 kg

[0034] Water-based color paste of various colors 2 kg Bentonite suspension 5 kg

[0035] Appropriate amount of water

[0036] Preparation method: Take stone powder, color paint film, water, and acrylic emulsion, stir and mix evenly, add alcohol ester-12, SN5040, bentonite suspension, NXZ, Huake-981, add titanium white paste and water-based color pastes, mix and stir , add water to adjust the viscosity to 20000P, and pack it.

Embodiment 2

[0038] Raw material formula:

[0039] Acrylic emulsion 65 kg Titanium white paste 0.5 kg

[0040] Polyvinyl alcohol hydrosol 3 kg Hydroxyethyl cellulose hydrosol 5 kg

[0041] Alcohol Ester-12 1kg SN5040 0.1kg

[0042] NXZ 0.1 kg Huake-981 1 kg

[0043] Thickener-1306 and HAS663 0.3 kg 60-200 mesh stone powder of various colors 18 kg

[0044] 60-120 mesh color paint film 1 kg 200-300 mesh stone powder of various colors 7 kg

[0045] Bentonite suspension 2 kg water appropriate amount

[0046] The preparation method is the same as in Example 1.

Embodiment 3

[0048] Raw material formula:

[0049] Acrylic emulsion 22 kg Titanium white paste 3 kg

[0050] Polyvinyl alcohol hydrosol 6 kg Hydroxyethyl cellulose hydrosol 15 kg

[0051] Alcohol Ester-12 1.5 kg SN5040 1 kg

[0052] NXZ 0.5 kg Huake-981 2 kg

[0053] Thickener-1306 and HAS663 0.5 kg 120-200 mesh stone powder of various colors 20 kg

[0054] 100-120 mesh color paint film 0.5 kg 200-300 mesh stone powder of various colors 20 kg

[0055] Water-based color paste 3 kg Bentonite suspension 3 kg

[0056] Appropriate amount of water

[0057] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a thin-layer multicolour sand textured architectural coating. Its formula composition includes the following components: (by wt%) 20-60% of various colour stone powders, 2-6% of polyvinyl alcohol hydrosol, 5-20% of hydroxyethyl cellulose hydrosol, 15-65% of film-forming resin emulsion, 0-10% of colour coating film, 0.5-1.5% of film-forming adjuvant, 0.5-10% of covering filling material, 2-5% of bentonite suspension, 0-5% of water-base various colour pastes and the rest is water.

Description

technical field [0001] The invention relates to a wall paint, in particular to a thin layer colorful sand wall paint with the color characteristics of latex paint. Background technique [0002] Sand wall paint is a thick layer of paint, commonly known as stone paint, also known as colored stone paint, real stone paint or imitation stone paint. It is a kind of resin emulsion film-forming material mixed with stone powder and stone particle fillers. Thick paint with imitation stone effect, the thickness of this thick paint is relatively large when decorating the wall, the general dosage is 1.5-5 kg / square meter, otherwise the hiding power will not meet the requirements, the color of the coating If it is not plump, there will be no stone-like effect. The color effects displayed by this kind of paint are all produced by the natural stone powder or the coloring of the paint after dyeing the stone powder, so only the color of the stone powder can not meet the performance requireme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D201/00C09D5/28C09D129/04C09D101/28
Inventor 巢启
Owner 巢启
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More