High ductility climate resistant solder stick with tensile strength of 600MPa

A technology with high tensile strength and high toughness, applied in the direction of welding medium, welding equipment, welding/cutting medium/material, etc., to achieve the effect of good atmospheric corrosion resistance, good low temperature impact toughness, and good comprehensive performance

Active Publication Date: 2007-03-07
BAOSHAN IRON & STEEL CO LTD +1
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a high-toughness weather-resistant electrode with a tensile strength of 600 MPa to solve the problem of matching manual electrodes for high-strength weather-resistant steel Q500NQR1 and Q550NQR1 with a tensile strength of 600 MPa

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] See Table 1 for coating formula examples, and the welding core is H08A; Table 2 shows the chemical composition of the electrode deposited metal.

[0027] Reality

apply

example

big

reason

stone

Fluorite

ferro-titanium

Alloy

medium carbon

Ferromanganese

45%

Ferrosilicon

synthesis

Mica

40 mesh

micro

silicon

pink

iron powder

gold

belongs to

chrome

copper powder

nickel powder

gold

belongs to

molybdenum

titanium

white

pink

1

39

16

11

5

2

3

3

9

1.6

1.0

1.7

0.5

2.0

2

40

18

10

4

1

3

2

11

1.0

0.7

2

0.5

4

3

41

19

9

4

1

2

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-flexibility welding bar whose tensile strength is 600MPa. Wherein, its components comprise that marble at 6-42;derbyshire spar at 16-22;ferrotitanium at 9-12;medium-carbon ferromanganese at 4-6; ferrosilicium at 1-3;synthetic mica at 1-3;micro silicon powder at 1-3;iron powder at 12-18;chrome metal at 1-2;copper powder at 0.5-1; nickel at 1-2;molybdenum at 0.3-0.8; and titanium white at 2-5. The inventive product has better corrosion resistance, with better low-temperature impact flexibility at -40Deg. C; and its yield strength is higher than 500MPa;tensile strength is higher than 600MPa; extensibility is higher than 20%;and (-40Deg. C) Akv>=60J.

Description

technical field [0001] The invention belongs to the field of welding materials, in particular to a high-strength, high-toughness weather-resistant welding rod. Background technique [0002] At present, there is no high-strength and high-toughness weather-resistant electrode with yield strength ≥ 500MPa, tensile strength ≥ 600MPa, and CVN impact toughness Akv ≥ 60J at -40°C. [0003] Weathering steel electrodes include: Cu-P, Cr-Cu, Ni-Cu, W-Cu, Cr-Ni-Cu alloy system. Cu-P series electrodes are less used because of their high P content, poor toughness and weldability; Cr-Cu, Ni-Cu, and W-Cu alloys are not well compatible with high-strength weathering steel Q500NQR1 and Q550NQR1 with a tensile strength of 600MPa matching. [0004] But there is currently no weathering steel electrode with a tensile strength of 600MPa. The Cr-Ni-Mo-Cu alloy system used in the patent of the present invention. Therefore, J606RH can be selected as the reference electrode. [0005] There is one...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23K35/22
Inventor 屈朝霞李自刚张汉谦侯永泰杨咏梅
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com