Scrape-wearable nanometer aqueous automobile paint preparation method

A water-based coating, scratch-resistant technology, applied in the direction of polyester coating, polyurea/polyurethane coating, coating, etc., to achieve excellent scratch resistance, easy to use, low VOC content effect

Active Publication Date: 2007-05-30
BASF COATINGS GMBH
View PDF0 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the invention is to overcome the defects of existing automotive coatings, to provide a scratch-resistant, stone-resistant water-based nano-auto coating and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Firstly, the composition formula of the selected automotive coating, wherein: the coating film-forming base material polyurethane acrylate consumption is 70%, the nano-powder titanium dioxide consumption is 8%, the solvent deionized water consumption is 21%, and the additive consumption is 1%.

[0021] Put titanium dioxide with an average particle size of 40nm in a container, then add dispersant TENLO 70, antifoaming agent polydimethylsiloxane, a certain amount of solvent deionized water, and pre-disperse it with a high-speed mixer for 10 minutes, then use Vibrated by a high-speed oscillator for 1 hour to obtain a nano-powder dispersion; add the nano-powder dispersion slurry to the coating film-forming base material polyurethane acrylate, and then add the film-forming aid Texanol alcohol ester and part of the remaining disinfectant Foaming agent polydimethylsiloxane was mixed, and then dispersed with a high-speed mixer for 30 minutes to obtain a nanocomposite emulsion; t...

Embodiment 2

[0024] The composition formula of selected coating in the present embodiment is basically the same as above-mentioned embodiment 1. But the nanometer powder adopts the titanium dioxide of 60nm, its consumption is 12wt%, and the consumption of film-forming base material urethane acrylate is 66wt%. The preparation process and steps of this example are completely the same as those of Example 1 above.

[0025] Spray the final prepared coating evenly on the tinplate with a film thickness of 25±5μm, and bake it at 60°C for 30 minutes to obtain the pre-coated plate sample B, which is reserved for performance evaluation test.

Embodiment 3

[0027] First, select the composition formula of the automotive coating, in which: the coating film-forming base material urethane acrylate dosage is 70%, the nano-powder silica dosage is 8%, the solvent deionized water dosage is 21%, and the additive dosage is 1 %.

[0028] Put silicon dioxide with an average particle size of 40nm in a container, then add dispersant TENLO 70, antifoaming agent polydimethylsiloxane, and a certain amount of solvent deionized water, and pre-disperse it with a high-speed mixer for 10 minutes, then Vibrate with a high-speed oscillator for 1 hour to obtain a nano-powder dispersion; add the nano-powder dispersion slurry to the coating film-forming base material polyurethane acrylate, then add the film-forming aid Texanol alcohol ester and part of the remaining The antifoaming agent polydimethylsiloxane was mixed, and then dispersed with a high-speed mixer for 30 minutes to obtain a nanocomposite emulsion; then the crosslinking agent butylated melamin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a making method of scraping-proof, stone-impacting resistant aqueous nanometer automobile paint in the chemical paint making technical domain, which comprises the following parts: 60-70% paint filming base, 5-15% nanometer powder, 20-25% solvent water and 0.5-1.0% adjuvant, wherein the adjuvant contains thickener, dispersant, defoamer and filming agent; the weight rate of crosslinking agent and nanometer emulsion is 0.9:1-1:1; the crosslinking agent is chemical material of melamine type; the scraping-proof index of paint layer can be 96-99% (displayed by glass keeping rate).

Description

technical field [0001] The invention relates to a preparation method of a scratch-resistant nanometer water-based automobile paint, which belongs to the technical field of chemical paint preparation technology. Background technique [0002] The car body is coated with a layer of paint film for protection and decoration, but during use, the car body often collides with hard objects. For example, when the car is running, it is hit by gravel on the road; when the car body is washed, impurities in the water wash away the paint film; it is also scratched by metal, branches and other objects, which affects the appearance of the car body. [0003] At the same time, as automotive coatings are becoming more environmentally friendly, water-based coatings with low VOC will become one of the mainstream automotive coatings in the future. Therefore, the development of water-based coatings with excellent scratch resistance and stone chip resistance has become an important topic for automo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D133/14C09D167/00C09D5/02B05D7/14
Inventor 施利毅张清涛张震宇杭建忠徐夏章
Owner BASF COATINGS GMBH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com