Resin tibetan style furniture surface material, decorative material and its preparation method
A decorative material and resin technology, applied in the field of decorative materials, can solve the problems of difficult to achieve the carving effect of Tibetan decorative materials, achieve low cost, strong antique and wood-like effects, and save wood
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0013] The invention discloses a method for preparing resin Tibetan furniture fabric or decorative material. The resin Tibetan furniture fabric or decorative material is composed of the following raw materials in percentage by weight: DC191 resin 55-80%; large white powder 20-40% ; accelerator 0.1-0.5%; curing agent 0.1-0.5%; Sexual story materials, Buddhist series story materials suitable for temple use are used as patterns on resin Tibetan furniture fabrics and decorative materials of the present invention; then the above series of patterns are drawn on wooden model boards, and the above-mentioned hollow patterns are hand-carved, and After the edge is polished and polished, it is sprayed with a bottom paint to make the model smooth; the preparation method of the resin Tibetan furniture fabric or decoration material comprises the following steps:
[0014] a) Mold making: Based on the wooden model, evenly prepare silica gel slurry with 99-99.5% silica gel and 0.5-1% mold curin...
Embodiment 1
[0026] Take the Tibetan-style series of stories suitable for home use and draw the 16th offering to the goddess pattern, draw it on the wood raw material model board, hand-carve out the above-mentioned hollow pattern, and polish and polish the edge and spray the base paint to make the model smooth;
[0027] Based on the wooden model, use 99 parts of silica gel and 0.5 parts of mold curing agent to evenly prepare a silica gel slurry; apply the prepared silica gel slurry evenly on the wooden model, and then apply a layer after the silica gel has solidified for 10 minutes. In this way, smear a total of 3 to 4 times to make a silicone mold. After the silicone mold is solidified, pour gypsum slurry on the silicone mold, and form a gypsum mold base after solidification;
[0028] The first pouring: Add 20 parts of white powder to 100 parts of DC191 resin, heat at 55°C, stir evenly, add 0.1 part of accelerator, stir evenly, then add 0.1 part of curing agent, pour DC191 resin slurry int...
Embodiment 2
[0033] Take all kinds of public welfare Tibetan-style story materials and Qisirui patterns suitable for public places, draw them on the wood raw material model board, carve out the above-mentioned hollow patterns by hand, grind and polish the edges, and spray the bottom to make the model smooth Qi;
[0034] Based on the wooden model, use 99.2 parts of silica gel and 0.8 parts of mold curing agent to evenly prepare silica gel slurry; spread the prepared silica gel slurry evenly on the wooden model, and then apply a layer after the silica gel has solidified for 15 minutes. In this way, smear a total of 3 to 4 times to make a silicone mold. After the silicone mold is solidified, pour gypsum slurry on the silicone mold, and form a gypsum mold base after solidification;
[0035]Mix DC191 resin, white powder, accelerator, and curing agent according to the above proportions. The first pour: Add 23 parts of white powder to 100 parts of DC191 resin, heat at 60°C, stir evenly, and add 0...