Poured epoxytar concrete material and its preparation process

An epoxy asphalt, pouring technology, used in roads, roads, buildings and other directions, can solve the problems of not particularly ideal low temperature performance, high mixing temperature, poor high temperature performance, etc., to achieve high temperature rutting resistance, low construction temperature, The effect of improving high temperature performance

Inactive Publication Date: 2009-12-16
重庆市智翔铺道技术工程有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] To sum up, the disadvantages of the existing epoxy asphalt concrete are: the low temperature performance is not particularly ideal, three times of rolling are required during paving, and the construction is complicated; the disadvantages of the cast asphalt concrete are poor high temperature performance, high mixing temperature, and waste of energy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0031] (1) Weigh raw materials according to the following ratio

[0032] A component: No. 90 asphalt 11 parts

[0033] Bisphenol A type epoxy resin E44 1.7 parts

[0034] Modified nonylphenol 3.4 parts

[0035] Cresyl glycidyl ether 0.1 parts

[0036] Component B: 0.8 parts of modified isophorone diamine

[0037] The total amount of stone basalt crushed stone and mineral powder is 83 parts

[0038] Stone particle size and dosage: the dosage of mineral powder is 24%, and the dosage of particle size 0-10mm is 76%.

[0039] (2) Preparation process

[0040] 1. Add No. 90 asphalt, bisphenol A epoxy resin E44, modified nonylphenol, and cresol glycidyl ether into a mixing pot, heat to 120°C, and stir and mix for 1 hour to obtain component A;

[0041] 2. Heat the stone to 160°C, add it into the mixing pot, and fully stir with component A for 5 minutes, keeping the temperature at 120°C;

[0042] 3. Heat component B to 130°C, add it to the mixture of stone and component A, fully ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to castable pavement materials. In view of the poor low-temperature performance of the existing epoxy asphalt concrete, it needs to be rolled three times during paving, and the construction is complicated; the cast-type asphalt concrete has poor high-temperature performance, high mixing temperature, and waste of energy. 1. Epoxy asphalt pouring concrete material and preparation method with convenient construction. The technical scheme adopted is: A component: 45-90 parts of asphalt, 4.5-36 parts of epoxy resin, 9-27 parts of modified alkylphenol; B component: curing agent; The ratio is 50:1 to 8:1; the ratio of stone to component A by mass is 9:1 to 3:1. Preparation method: Add asphalt, epoxy resin, and modified alkylphenol into the mixing pot according to the mass ratio, stir at 120-160°C, then add the heated stone and stir, and finally add the heated curing agent and stir, keep it warm for 0-160°C 120 minutes to get the product.

Description

1. Technical field [0001] The invention relates to a novel pouring pavement material, in particular to an epoxy asphalt pouring concrete material and a preparation method thereof. 2. Background technology [0002] With the continuous growth of traffic volume and the obvious increase of axle load, as well as the channelization of high-grade highway traffic vehicles, asphalt concrete pavement is facing new severe challenges, especially the traditional continuous graded asphalt concrete pavement is challenged. Some highways have been damaged to varying degrees within one or two years of opening to traffic, seriously affecting the function and life of the road surface. This is because the viscoelastic properties of the asphalt pavement itself determine its inevitable shortcomings: (1) the thermoplasticity of the asphalt causes irreversible permanent deformation of the asphalt pavement, such as rutting, pushing, etc.; (2) the asphalt pavement is susceptible to natural deformation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00E01C3/02
CPCC04B26/26
Inventor 张华徐光红陈仕周曹雪娟皮育晖
Owner 重庆市智翔铺道技术工程有限公司