High flexible flame retardant PC(polycarbonate)/ABS alloy

A high toughness, alloy technology, applied in the field of thermoplastic resin composition, can solve the problems of easy stress cracking, poor processing fluidity, easy wear, etc., and achieve the effect of reducing melt viscosity and improving processing performance

Inactive Publication Date: 2007-07-25
MITAC PRECISION TECH CO LTD SHUNDE DISTRICT FOSHAN CITY
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] PC also has some obvious defects, such as: poor processing fluidity, easy stress cracking, sensitive to notch, easy to wear, poor chemical resistance, high price, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] Take PC recycled materials, ABS, grafts, MBS, epoxy resin, antioxidant, flame retardant and other components, and blend all the raw materials according to the following composition formula:

[0060] (a) 59 pieces of recycled PC materials

[0061] (b) ABS 20 parts

[0062] (c) 4 parts of ABS-g-MAH

[0063] (d) 5 copies of MBS

[0064] (e) 0.5 parts of epoxy resin

[0065] (f) Antioxidant 2921 0.2 parts

[0066] (g) 9 parts of triphenyl phosphate

[0067] (h) 1.5 parts of antimony trioxide

[0068] (i) 1.5 parts of zinc borate

[0069] (j) 0.5 parts of polytetrafluoroethylene

[0070] Then the blended material is kneaded and granulated in an extruder, and the resulting kneaded and granulated product is made into a finished product by injection molding. Finally, the mechanical properties of the finished product are tested according to the national standard GB13525 / T-92, and its melting Index (MI) and its flame retardant performance tested according to the American ...

Embodiment 2

[0074] Take PC recycled materials, ABS, grafts, MBS, epoxy resin, antioxidant, flame retardant and other components, and blend all the raw materials according to the following composition formula:

[0075] (a) 51 pieces of recycled PC materials

[0076] (b) ABS 35 parts

[0077] (c) ABS-g-MAH 3 parts

[0078] (d) 3 copies of MBS

[0079] (e) 0.8 parts of epoxy resin

[0080] (f) Antioxidant 2921 0.3 part

[0081] (g) 6 parts of triphenyl phosphate

[0082] (h) 1 part antimony trioxide

[0083] (i) 1 part zinc borate

[0084] (j) 0.8 parts of polytetrafluoroethylene

[0085] Then the blended material is kneaded and granulated in an extruder, and the resulting kneaded and granulated product is made into a finished product by injection molding. Finally, the mechanical properties of the finished product are tested according to the national standard GB13525 / T-92, and its melting Index (MI) and its flame retardant performance tested according to the American Electrotechnical A...

Embodiment 3

[0089] Take PC recycled materials, ABS, grafts, MBS, epoxy resin, antioxidant, flame retardant and other components, and blend all the raw materials according to the following composition formula:

[0090] (a) 45 copies of recycled PC materials

[0091] (b) ABS 27 parts

[0092] (c) ABS-g-MAH 3 parts

[0093] (d) 9 copies of MBS

[0094] (e) 0.5 parts of epoxy resin

[0095] (f) Antioxidant 2921 0.3 parts

[0096] (g) 12 parts of triphenyl phosphate

[0097] (h) 2 parts of antimony trioxide

[0098] (i) Zinc borate 2 parts

[0099] (j) 0.3 parts of polytetrafluoroethylene

[0100] Then the blended material is kneaded and granulated in an extruder, and the resulting kneaded and granulated product is made into a finished product by injection molding. Finally, the mechanical properties of the finished product are tested according to the national standard GB13525 / T-92, and its melting Index (MI) and its flame retardant performance tested according to the American Electrote...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Impact strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Bending strengthaaaaaaaaaa
Login to View More

Abstract

This invention relates to a formula for preparing flame-retardant PC / ABS alloy with high toughness by modifying recovered PC. The formula comprises: recovered PC 45-60 parts, ABS 20-35 parts, grafting monomer 1-5 parts, acrylate copolymer 3-10 parts, epoxy resin 0.1-1 part, antioxidant 0.1-0.5 part, plasticizer 6-15 parts, stibium series flame retardant 1-3 parts, inorganic flame retardant 1-3 parts, and polytetrafluoroethylene 0.2-0.8 part. This invention adopts high-efficiency compatibilizer to modify recovered PC and ABS and prepare PC / ABS alloy, thus can reduce the melt viscosity of PC and improve its processability, and is environmentally friendly due to resue of recovered PC.

Description

technical field [0001] The invention relates to the field of thermoplastic resin compositions in polymer material technology, in particular to a formula for modifying PC (Polycarbonate, polycarbonate) recycled materials into high-toughness flame-retardant PC (polycarbonate) / ABS alloys. Background technique [0002] PC is an engineering plastic with superior comprehensive performance. It has excellent impact toughness, dimensional stability, electrical insulation, creep resistance, weather resistance, transparency and non-toxicity. It is widely used in mechanical equipment, construction engineering, Transportation, instrumentation and electrical and electronic lighting and other fields. [0003] PC also has some obvious defects, such as: poor processing fluidity, easy stress cracking, sensitive to notch, easy to wear, poor chemical resistance, high price, etc. The consumption of PC is large, and at the same time, the amount of secondary materials, nozzle materials and recycl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L69/00C08K5/524C08L55/02C08L33/04C08L63/00C08L27/18
Inventor 汪克风岳瑟杨得志
Owner MITAC PRECISION TECH CO LTD SHUNDE DISTRICT FOSHAN CITY