Novel environment-protection stereo brocade modified coating
A modified and environmentally friendly technology, applied in coatings and other directions, can solve the problems of laborious, various needs, and increased decoration costs.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment approach 1
[0017] The parts by weight of various materials for making the new environment-friendly three-dimensional brocade modified coating are: 18 parts of water, 0.2 parts of dispersant DA-01, 0.1 part of wetting agent OP-10, 10 parts of pearl powder, 0.4 parts of defoamer, 0.8 parts of alcohol ester-12, 0.2 parts of antiseptic and bactericide, 0.1 parts of thickener, 0.2 parts of AMP-95, 38 parts of styrene-acrylic emulsion, 5 parts of 2% hydroxyethyl cellulose solution, 25 parts of 801 modified glue, propylene glycol 2 parts, appropriate amount of color paste. The defoamer here is used in combination with silicone defoamer or tributyl phosphate, and the thickener is an associative polymer thickener. The required color paste is determined to be added according to the actual color depth.
[0018] The production method is:
[0019] 1. Mix 2% hydroxyethyl cellulose solution with water and dissolve it 2-3 hours in advance for later use.
[0020] 2. Add dispersant DA-01, wetting agent...
Embodiment approach 2
[0027] The parts by weight of various materials for making the new environment-friendly three-dimensional brocade modified coating are: 18 parts of water, 0.2 part of dispersant orotan731a, 0.1 part of wetting agent X-405, 10 parts of pearl powder, 0.4 part of defoamer, alcohol ester 0.8 parts of -12, 0.2 parts of antiseptic and bactericide, 0.1 parts of thickener, 0.2 parts of ammonia water, 38 parts of styrene-acrylic emulsion, 5 parts of 2% hydroxyethyl cellulose solution, 25 parts of 801 modified glue, 2 parts of ethylene glycol , appropriate amount of color paste. The defoamer here is used in combination with silicone defoamer or tributyl phosphate, and the thickener is an associative polymer thickener. The required color paste is determined to be added according to the actual color depth.
[0028] The production method is:
[0029] 1. Mix 2% hydroxyethyl cellulose solution with water and dissolve it 2-3 hours in advance for later use.
[0030] 2. Add dispersant orotan...
Embodiment approach 3
[0037] The parts by weight of various materials for making the new environment-friendly three-dimensional brocade modified coating are: 18 parts of water, 0.2 part of dispersant 1124, 0.1 part of wetting agent CF-10, 10 parts of pearl powder, 0.4 part of defoamer, alcohol ester 0.8 parts of -12, 0.2 parts of antiseptic and bactericide, 0.1 parts of thickener, 0.2 parts of ammonia water, 38 parts of pure acrylic emulsion, 5 parts of 2% hydroxyethyl cellulose solution, 25 parts of 801 modified glue, 2 parts of propylene glycol, color Appropriate amount of pulp. The defoamer here is used in combination with silicone defoamer or tributyl phosphate, and the thickener is an associative polymer thickener. The required color paste is determined to be added according to the actual color depth.
[0038] The production method is:
[0039] 1. Mix 2% hydroxyethyl cellulose solution with water and dissolve it 2-3 hours in advance for later use.
[0040]2. Add dispersant 1124, wetting age...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com