Poly (hexanediamine adipate) and polyphthalamide fiber-adding alloy and preparation method thereof

A technology of polyhexamethylene adipate and polyphthalamide, which is applied in the direction of drug combinations, pharmaceutical formulas, and medical preparations containing active ingredients, can solve the problems of high cost and low flow performance of PPA, and achieve Effect of controlling processing cost and improving surface quality

Inactive Publication Date: 2008-01-09
SHENZHEN KEJU NEW MATERIAL
View PDF1 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to overcome the disadvantages of high cost of traditional materials and low flow performance of PPA alone, and provide a polyadipate adipate that improves the surface quality of products and effectively controls the processing costs of materials and product production. Amine and polyphthalamide fiber-reinforced alloy and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Poly (hexanediamine adipate) and polyphthalamide fiber-adding alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] According to the percentage by weight, PA66 46.15%, PPA 20%, lubricant zinc stearate 0.15%, antioxidant (triethylene glycol bis-3-(3-tert-butyl-4-hydroxyl-5-methylphenyl) Acrylonitrile and tris (2,4-di-tert-butylphenol) phosphite (mixed in a ratio of 1:1) 0.2%, phase solvent (Y-aminopropyltriethoxysilane) 0.5%, pre-mixed in a mixing tank After 6 minutes, extrude and granulate through twin-screw, and add 33% of long glass fibers at the same time. Its processing technology is 265-275℃ in the first zone, 275-290℃ in the second zone, 280-300℃ in the third zone, 280-300℃ in the fourth zone, 280-300℃ in the fifth zone, 275-295℃ in the sixth zone, and 270-270 in the seventh zone. 290°C.

Embodiment 2

[0036] According to the percentage by weight, PA66 41.15%, PPA 25%, lubricant zinc stearate 0.15%, antioxidant (triethylene glycol bis-3-(3-tert-butyl-4-hydroxyl-5-methylphenyl) Acrylonitrile and tris (2,4-di-tert-butylphenol) phosphite (mixed in a ratio of 1:1) 0.2%, phase solvent (Y-aminopropyltriethoxysilane) 0.5%, pre-mixed in a mixing tank 6 minutes, and then granulated by twin-screw extrusion, while adding 33% of long glass fibers. Its processing technology is 265-275℃ in the first zone, 275-290℃ in the second zone, 280-300℃ in the third zone, 280-300℃ in the fourth zone, 280-300℃ in the fifth zone, 275-295℃ in the sixth zone, and 270-270 in the seventh zone. 290°C.

Embodiment 3

[0038] According to the percentage by weight, PA66 44.65%, PPA25%, lubricant zinc stearate 0.15%, antioxidant (triethylene glycol bis-3-(3-tert-butyl-4-hydroxyl-5-methylphenyl) propene Nitrile and three (2,4-di-tert-butylphenol) phosphite (mixed in a ratio of 1:1) 0.2% were pre-mixed in a mixing tank for 6 minutes, and then granulated by twin-screw extrusion, while adding long glass fiber 30 %. Its processing technology is 265-275℃ in the first zone, 275-290℃ in the second zone, 280-300℃ in the third zone, 280-300℃ in the fourth zone, 280-300℃ in the fifth zone, 275-295℃ in the sixth zone, and 270-270 in the seventh zone. 290°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention is concerned with alloy with fibre made of poly(hexamethylene adipamide) and phthalamide phthalic diamide. It relates to 36.15 to 46.15 percent of poly (hexamethylene adipamide), 20 to 30 percent of phthalamide phthalic diamide (PPA), 30 to 33 percent of long fiberglas, 0.1 to 0.2 percent of lubricant and 0.1 to 0.3 percent of antioxidant in weight proportion. This also shows the preparation method of the said alloy. This product and method can improve the surface quality and control the cost of material and product, and it is fit for the high demand of heat resisting, such as engine accessory, dynamoelectric tool shell, inside and outside parts of electrical apparatus with and details of cars.

Description

technical field [0001] The invention relates to a polyhexamethylene adipate and polyphthalamide fiber-added alloy, in particular to a polyhexamethylene adipate which improves the surface quality of products and effectively controls the processing cost of materials and product production. Amine and polyphthalamide-added fiber alloy and its preparation method, the material of the invention is mainly used for mechanical parts with high heat resistance requirements, electric tool shells, internal and external parts of electrical appliances, auto parts and the like. Background technique [0002] At present, the domestically produced polyhexamethylene adipate (PA66) plus glass fiber modified materials are made of pure PA66 plus glass fiber or PA66 and polycaprolactam (PA6) blended with glass fiber. The advantages of this type of material Some materials have good flow properties and are easy to process and shape, but some high-end heat-resistant materials cannot meet the product re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K36/896A61K36/8969A61P17/00A61K35/56A61K35/58C08K5/544C08K7/14C08K13/04C08L77/06
Inventor 徐东贺永王贤文
Owner SHENZHEN KEJU NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com