Special-purpose grease for powdery emulsifying explosive
A technology for powder emulsion explosives and special grease, applied in the field of special grease for explosives, can solve the problems of poor production environment, fluctuation of quality, high labor intensity of workers, etc., to reduce production costs, solve the trouble of purchasing and use, and high labor intensity Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0013] Embodiment 1: Take by weighing 30g of paraffin wax, 32g of microcrystalline wax and heat and melt or directly add to the beaker, add the above-mentioned beaker after breaking or heating and melting the 40g of rosin that weighed, and then add 8g of mineral oil to the second-line wax paste, 10g of mineral oil to light Dewaxing paste (the components of the wax paste are kept warm in a storage tank and partially dehydrated before adding to the beaker), put 2g of Siben-80 into the above beaker, start stirring until completely dissolved, and the stirring speed is 100 rpm . Raise the temperature to 110°C and keep it for 0.5hr, then cool it down, then test its melting drop point, viscosity and cone penetration, etc., then filter to remove impurities in the mixture, and finally put the wax liquid into a fixed container to cool and form ,Package.
Embodiment 2
[0014] Embodiment 2: take by weighing 35g paraffin wax, 25g microcrystalline wax heating and melting or directly add beaker, add above-mentioned beaker after the 45g rosin that weighs is crushed or heating and melting, then add 10g mineral oil to second-line wax paste (this wax paste group Before adding to the beaker, it is placed in a storage tank to keep warm and partially dehydrated), 10g wax base oil, and 0.5 Siben-80 are put into the above-mentioned beaker, and start stirring until completely dissolved, and the stirring speed is 100 rpm. Raise the temperature to 110°C and keep it for 0.5hr, then cool it down, then test its melting drop point, viscosity and cone penetration, etc., then filter to remove impurities in the mixture, and finally put the wax liquid into a fixed container to cool and form ,Package.
Embodiment 3
[0015] Embodiment 3: Take by weighing 25g of paraffin wax, 35g of microcrystalline wax and heat and melt or directly add to the beaker, add the above-mentioned beaker after the 50g of rosin that weighs is crushed or heat and melt, then add 5g of mineral oil to the second-line wax paste, 10g of mineral oil to Four-line wax paste (this wax paste component is placed in a storage tank to keep warm and partially dehydrated before being added to the beaker), 2g of polyisobutylene succinimide, put into the above-mentioned beaker, start stirring until it is completely dissolved, and the stirring speed at 100 rpm. Raise the temperature to 110°C and keep it for 0.5hr, then cool it down, then test its melting drop point, viscosity and cone penetration, etc., then filter to remove impurities in the mixture, and finally put the wax liquid into a fixed container to cool and form ,Package.
PUM
Property | Measurement | Unit |
---|---|---|
cone penetration | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com