A technology of metallized pellets and drying furnaces, applied in drying, dryers, furnaces, etc., can solve the problems of pellet fragmentation and limited production efficiency, and achieve cost saving, good replaceability, and drying high efficiency effect

Inactive Publication Date: 2008-03-05
大连熔融还原设备制造有限公司
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

To dry the pellets with high water content, since the pellets are heated externally, there are strict requirements on the drying speed. If the drying speed is too fast, the pellets will

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Drying furnace of metallization ball and drying method thereof
  • Drying furnace of metallization ball and drying method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0035] Now in conjunction with accompanying drawing, the present invention is further described as follows:

[0036] As shown in Fig. 1 and Fig. 2, the drying furnace of the metallized pellets has an annular furnace body and an annular furnace bottom, and the inner side of the furnace body is lined with an insulating material, so that the sides and the upper part of the furnace body are closed. The upper part of the furnace body is equipped with a bellows, the lower part of the furnace body is matched with the annular furnace bottom, sealed with sand, and equipped with a windshield;

[0037] The annular furnace bottom constitutes an annular gas outlet box, steel grids are placed on the top of the furnace bottom, the inner ring side wall of the furnace bottom is connected with the rotating flue, and the bottom of the furnace bottom is fixedly connected with two sets of coaxial box-shaped steel boxes with different radii. Structural support beams, ring-shaped tracks are fixedly ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a metallized pellet drying furnace and drying method. Its drying heating source is rotary hearth furnace flue gas; the temperature of flue gas is 300-350 degrees centigrade. The drying process is following: putting the pellets uniformly on steel grid by distributing device; starting driving system; support wheel group rotating; matched rail, box-shape support beam connected with the rail and ring shaped hearth rotating together around central shaft, the steel grid rotating synchronically along with the hearth; the said flue gas entering into air box via.

Description

technical field [0001] The invention relates to a drying equipment for the iron and steel industry, in particular to a drying furnace for metallized pellets. Background technique [0002] Pellet drying is an intermediate operation before entering the rotary hearth furnace for the smelting reduction stage. The purpose is to enable the dried pellets to safely withstand the temperature stress during the preheating phase of the rotary hearth furnace. The pellets added with bentonite contain 10%-15% water. On the one hand, these moisture can lead to plastic deformation of the pellets, and on the other hand, due to the influence of the "cracking temperature" (generally 400-450°C) of the pellets, it will cause cracks in the preheating stage (preheating temperature is higher than 900°C). or "burst". Therefore, before the pellets enter the smelting reduction stage, drying must be carried out to make the moisture content below 3%, so as to meet the requirements of the process. [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): F26B17/32F26B3/06
Inventor 张宜平赵国顺徐绍德
Owner 大连熔融还原设备制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap