Weather-resistant hot rolled broad steel strip and method for manufacturing same

A manufacturing method and weather-resistant technology, applied in the field of weather-resistant steel and its manufacture, and weather-resistant hot-rolled wide steel strip, can solve the problems of difficulty in marketing and high cost, and achieve good atmospheric corrosion resistance, low cost, and no reduction in corrosion resistance Effect

Inactive Publication Date: 2008-03-12
LAIWU IRON & STEEL GRP
View PDF3 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The cost of this invention is very high, and it is difficult to promote it in the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Embodiment 1: weather-resistant hot-rolled wide steel strip and its manufacturing method

[0032] 1. The chemical composition of steel is as follows by weight percentage:

[0033] C: 0.08%, Si: 0.38%, Mn: 0.38%, P: 0.086%, S: 0.005%, Cu: 0.263%, Cr: 0.349%, Ni: 0.125%, Alt: 0.021%, the rest is Fe and not Avoid impurities.

[0034] 2. Manufacturing method of weather-resistant hot-rolled wide steel strip

[0035] (1) Production process

[0036] Hot metal pretreatment - top and bottom double blowing converter smelting - LF ladle refining - slab continuous casting - 1500 wide strip rolling (2) Taking a 6.0mm thick steel strip as an example, the thickness of the cast slab is 160mm, which is a medium-thin slab. Proceed as follows:

[0037]Hot metal pretreatment: Control the sulfur in the hot metal below 0.010%, the temperature is not lower than 1250°C, and remove the slag on the surface of the hot metal after desulfurization. Converter smelting endpoint control: C: 0.04%...

Embodiment 2

[0039] Embodiment 2: weather-resistant hot-rolled wide steel strip and its manufacturing method

[0040] 1. The chemical composition of steel is as follows by weight percentage:

[0041] C: 0.07%, Si: 0.35%, Mn: 0.38%, P: 0.089%, S: 0.006%, Cu: 0.281%, Cr: 0.375%, Ni: 0.133%, Alt: 0.015%, the rest is Fe and not Avoid impurities.

[0042] 2. The manufacturing method of the weather-resistant hot-rolled wide steel strip, the production process is the same as in Example 1.

[0043] Taking the 3.8mm thick steel strip as an example, the casting slab has a thickness of 160mm, which is a medium-thin slab. Proceed as follows:

[0044] Hot metal pretreatment: Control the sulfur in the hot metal below 0.010%, the temperature is not lower than 1250°C, and remove the slag on the surface of the hot metal after desulfurization. Converter smelting endpoint control: C: 0.04%, S: 0.010%. LF refining white slag operation. Each heat of molten steel is fed into a 500mSi-Ca line for calcifica...

Embodiment 3

[0047] 1. The chemical composition of steel is as follows by weight percentage:

[0048] C: 0.08%, Si: 0.37%, Mn: 0.4%, P: 0.094%, S: 0.008%, Cu: 0.307%, Cr: 0.338%, Ni: 0.126%, Alt: 0.015%, the rest is Fe and not Avoid impurities.

[0049] Manufacturing method is the same as embodiment 1.

[0050] The performance data of the wide steel strip is listed in Table 1, and the relevant test methods adopt international general standards:

[0051] Table 1

[0052]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a manufacturing method of a weathering resistance steel stripe, whose chemical components by weight are: C 0.06-0.12%, Si 0.25-0.50%, Mn 0.30-0.50%, P 0.07-0.15%, S 0.015% below, Cu 0.25-0.40%, Cr 0.30-1.2%, Ni 0.10-0.50%, and the remainder Fe and unavoidable foreign matters. The steel stripe is manufactured by converter smelting, continuous sheet blank casting, and rolling by a hot continuous rolling unit, etc., is of excellent anti-corrosion performance and weldability, even mechanical properties, and can be used for making a plurality of products with long service life. The weathering resistance steel stripe is specially suitable for manufacturing containers, and is of low cost and easy to industrialize.

Description

technical field [0001] The invention relates to a weather-resistant steel and a manufacturing method thereof, belonging to the field of low-alloy steel manufacturing, in particular to a weather-resistant hot-rolled wide steel strip mainly used for container manufacturing. Background technique [0002] Weathering steel is a general term for a class of steel resistant to atmospheric corrosion. The existing technology generally uses a large amount of alloying elements such as Cu, P, Cr, Ni, Al, etc. to the steel, and some also add As, Ce, Co, Ti, V and other elements. Such as Chinese patent documents CN1752260 and CN1970818, although the performance of steel has been improved like this, the cost is too high, and the technological process is complicated, and there is great difficulty in marketization. [0003] Chinese patent document CN1664152 discloses a highly strong corrosion-resistant steel plate for railway vehicles (hereinafter referred to as steel type 1) and its prepara...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/42C22C33/04B21B1/46B21B37/74B21C47/02C21C7/064C21C7/06C21C7/072B22D11/16C21D8/02
Inventor 董杰周平亓伟伟王学新孙正旭霍孝新宁伟杨旭胡滨陈爱娇
Owner LAIWU IRON & STEEL GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com