Water emulsion coating and preparation method thereof

A water-based latex and coating technology, applied in latex paints, coatings, etc., can solve the problems of coating syneresis and affect the appearance of coatings, and achieve the effect of good thixotropy

Inactive Publication Date: 2011-05-25
SHENZHEN OCEANPOWER NEW MATERIALS TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As far as the paint itself is concerned, the use of hydratable cellulose ethers and alkali-swellable emulsions to form a large volume limits flocculation, resulting in severe syneresis and delamination of the paint during storage and transportation, which affects the appearance of the paint.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water emulsion coating and preparation method thereof
  • Water emulsion coating and preparation method thereof
  • Water emulsion coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] High PVC coating in styrene-acrylic emulsion (PVC=45%, solid NVW=60%)

[0033] Raw materials Parts by weight Remarks

[0034] water 18.85

[0035] Propylene Glycol 2.0

[0036] Dispersant with association (H-34) 1.5

[0037] Wetting agent (Hydropalant 436) 0.1

[0038] Preservative (Alex251) 0.15

[0039] Defoamer ( A10) 0.3

[0040] PH regulator (AMP95) 0.1

[0041] Rutile titanium dioxide (R-706) 16.0 DuPont

[0042] Filler 1 (heavy calcium-1000 mesh) 5.0 Jiaoling Guangfu

[0043] Filler 2 (wollastonite-800 mesh) 5.0

[0044] Filler 3 (kaolin DB80) 5.0 Shanxi Jinyang

[0045] Filler 4 (BaSO 4 -250 mesh) 14.0 Xinji, Hebei

[0046] Styrene-acrylic emulsion RS-998A 30.0

[0047] Coalescing agent (alcohol ester twelve) 1.5

[0048] Associative thickener HEUR (DSX3551) 0.55

[0049] Preparation:

[0050] 1. Grinding slurry preparation: leave about 4 parts of water in advance, put the remaining water and alcohol solvent into the dispersion tank, disperse at...

Embodiment 2

[0059] Embodiment 2 and list of traditional paint raw materials:

[0060]

Example 2

Market Traditional Method Recipe

Coating Raw Materials

parts by weight

parts by weight

water

21.7

22.4

Propylene Glycol

2.0

1.5

[0061] Preservatives (Alex251)

0.15

0.15

Dispersant with association (Hydropalat 100)

1.0

/

Conventional hydrophilic dispersant (Hydropalat 5040)

0.15

0.5

Wetting agent (Hydropalat 436)

0.1

0.1

Defoamer (F-155)

0.3

0.3

Rutile titanium dioxide (R215)

18.0

18.0

Filler 1 - heavy calcium

15.0

15.0

Filler 3 - Kaolin

8.0

8.0

Filler 5-Talc powder

2.0

2.0

Styrene acrylic emulsion 296D

30.0

30.0

Coalescing agent (alcohol ester-12)

1.5

1.5

PH adjuster (AMP-95)

0.1

0.1

HEUR associative thickener 1 (...

Embodiment 3～5

[0071] Embodiment 3~5 raw material list:

[0072]

[0073]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aqueous latex paint with high solid and low-viscosity, wherein the coating viscosity is regulated by associative thickeners, such as hydrophobic modified polyaminoester HEUR, hydrophobic modified Polyether HPE and / or hydrophobic modified alkaline expansive emulsion HASE, and the pigment and filler ground paint-pulp is dispersed by associative dispersants, and the moderate-high-low PVC aqueous latex paint used is 20-60 percent in total paint by weight of bonding emulsion. In the invention, the organic pigment and filler particle surface is modified by associative dispersant to enable the organic pigment and filler particle surface to be drawn into the thickening-network, so as to meet requires for lower shear viscosity of the coating and direct construction without dilution with water. The coating abandons conventional hydration thickening method, and all adopts associative thickeners to regulate the coating viscosity, so the coating has good low thixotropy; while the bonding latex particles and pigment and filler particle with function of fill and color are homogeneously distributed more ideally, therefore the coating has no layer phenomenon appeared which is caused by syneresis.

Description

【Technical field】 [0001] The invention relates to a water-based latex paint and a preparation method thereof, in particular to a high-solid low-viscosity water-based latex paint and a preparation method thereof. 【Background technique】 [0002] The coating industry puts forward requirements for the development of coating technology, requiring coatings to improve performance, reduce volatile matter, and reduce organic solvent emissions. Therefore, high-solid, 100% solid powder coatings, light-curing, and environmentally friendly water-based coatings are the development direction of the coatings industry. [0003] At present, the solid content of coatings formulated in the market is generally lower than 60%, even lower than the national standard requirement of 45%. The viscosity of the coating is too high. In order to meet the low viscosity requirements of construction, a large amount of water is added to further reduce the effective film-forming substances and reduce the thickn...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D5/02C09D7/12
Inventor 陈素平何唯平
Owner SHENZHEN OCEANPOWER NEW MATERIALS TECH