A manufacturing method and technology of blades, applied in the direction of manufacturing tools, knives for shearing machine devices, shearing devices, etc., to achieve the effect of improving hardenability and improving wear resistance
Inactive Publication Date: 2008-03-19
BAOSHAN IRON & STEEL CO LTD +1
View PDF1 Cites 46 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The blade material belongs to micro-alloyed tool steel, which is only suitable for ordinary mechanical blades
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0042] Embodiment sees table 2, table 3.
[0043] Table 2 (Wt.%)
[0044] C
Si
mn
Ni
Cr
Mo
V
P
S
Example 1
0.70
1.20
0.48
4.50
0.50
0.30
0.015
0.008
Example 2
0.50
1.00
0.35
5.10
1.40
1.00
0.015
0.008
Example 3
0.55
0.50
0.20
5.50
2.00
1.50
0.015
0.008
Example 4
0.55
0.70
0.50
5.20
1.00
0.80
0.015
0.008
Example 5
0.40
0.80
0.40
4.00
0.80
1.20
0.015
0.008
Example 6
0.55
0.60
0.40
6.00
0.80
0.50
0.015
0.008
comparative example
0.45
0.30
0.30
4.10
1.40
0.25
0.015
0.008
[0045] The difference between the comparative example and th...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
hardness
aaaaa
aaaaa
Login to view more
Abstract
The present invention discloses a flying shear blade. The component has the weight percentage that C is 0.40-0.70, Si is 0.50-1.20, Mn is 0.20-0.50, Cr is 4.00-6.00, Mo is 0.50-2.00, V is 0.30-1.50, P is less than or equal to 0.02, S is less than or equal to 0.02, and Fe and inevitable impurity are the residual. The present invention provides a manufacture method of electric furnace smelting, and ingot casting; hydrogen removing and annealing treatment, and forging; preliminary heat treatment, rough machining, quenching and tempering heat treatment (primary quenching and high temperature tempering), semi finishing, ultimate heat treatment (secondary quenching, primary low temperature tempering, and secondary low temperature tempering), and fine finishing. By effectively controlling the material texture and the morphology, the quantity, the size and the distribution of carbonide, the quenching temperature and the tempering temperature of the quenching and tempering heat treatment, and the quenching temperature and the tempering temperature of the ultimate heat treatment are controlled, the texture crystal grains are more refined, the carbonide is distributed in a dispersed way, and simultaneously, the thermal stability and the retentivity are remarkably enhanced, thereby being advantageous for improving the operational performance of the blade.
Description
technical field [0001] The invention relates to the field of metallurgical tool materials, in particular to a flying shear blade suitable for cutting hot-rolled high-strength thick plates to length or multiple lengths and a manufacturing method thereof. Background technique [0002] With the rapid development of my country's railways, bridges, construction, petroleum, automobiles, and household appliances, the proportion of high-strength hot-rolled commercial materials continues to increase, including: pipeline steel, automobile girder plates, high-strength container plates, high-strength engineering machinery steel, Tool steel, knife die saw blade steel and other series of varieties. [0003] Due to the high internal stress of the high-strength plate incoming material, poor plate shape and cross-section quality, shearing production is difficult, and it is easy to cause chipping, uneven wear and rapid passivation of the shearing blade, resulting in frequent shutdowns to repla...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more