Grinding method for high-grade stainless steel frosted plate surface

A stainless steel and frosted plate technology, which is applied in grinding/polishing equipment, grinding machines, abrasive belt grinders, etc., can solve the problems of poor surface quality, no suitable method, and no method to adjust the grain size of the abrasive belt, etc., to increase the grinding speed. Yield, improvement of surface quality, effect of defect reduction

Inactive Publication Date: 2008-04-30
SHANXI TAIGANG STAINLESS STEEL CO LTD
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the production process of the existing high-grade stainless steel frosted plate, the grinding method of the surface of the stainless steel frosted plate does not have an abrasive belt suitable for grinding stainless steel plate, and there is no method to adjust the grain size of the abrasive belt and a reasonable grinding speed. The quality of the surface does not meet the requirements, the surface quality is poor, and there are many defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Grinding method for high-grade stainless steel frosted plate surface

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] What this embodiment grinds is 304 for domestic high-grade stainless steel grinding plate, and its surface quality is N0.4, see Fig. 1, steel plate surface roughness R a The value of 0.04 ~ 0.06. The width is 1000mm, and the finished product thickness is 1.2mm.

[0040] (1) Raw material shot blasting

[0041] 1. Stop adding new steel shot 5 hours before sending the steel strip after raw material annealing, cooling and scale breaking to the shot blasting machine of the production unit.

[0042] 2. The present embodiment is a narrow-width raw material. When the raw material is shot blasted, it adopts low-speed shot blasting under the premise of cleaning the surface (without residual scale on the surface). min.

[0043] 3. The surface has no deep defects and is suitable for the production of raw material coils for frosted boards. The inspectors of each raw material annealing and pickling unit will stamp the seal "Special Material for Frosted Boards" on the upper left co...

Embodiment 2

[0052] What this embodiment grinds is 304 domestic high-grade stainless steel frosted plates, and its surface quality is N0.4. The difference between this embodiment and embodiment 1 is that the third grinding head is installed with a cumulative decay time of 420min. Abrasive belt. Other steps are the same as those in Embodiment 1.

Embodiment 3

[0054] What the present embodiment grinds is 304 for export high-grade product stainless steel abrasive plate, and its surface quality is No. ) See Figure 2, steel plate surface roughness R a The value of 0.06 ~ 0.08. The width is 1300mm, and the finished product thickness is 1.0mm.

[0055] (1) Raw material shot blasting

[0056] 1. Five hours before the raw material annealed, cooled and scale-broken steel plate is sent to the shot blasting machine of the production unit, the shot blasting machine stops adding new steel shots.

[0057] 2. This embodiment is for wide-width raw materials. When the raw materials are shot blasting, the speed of the blasting head is adjusted according to the deceleration ratio of the narrow-width raw materials.

[0058] 3. The surface has no deep defects and is suitable for the production of raw material coils for frosted boards. The inspectors of each raw material annealing and pickling unit will stamp the seal "Special Material for Frosted Bo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Widthaaaaaaaaaa
Thicknessaaaaaaaaaa
Widthaaaaaaaaaa
Login to View More

Abstract

Provided is a grinding method of the surface of a high-grade stainless steel frosted plate. The steps of grinding method include that, (1) throwing pills, firstly, after a steel plate is annealed, cooled and scale broken, the steel plate is taken into a pill throwing machine, new steel pills are stopped from being added at the time of five hours earlier of the steel plate being taken into the pill throwing machine, then, when narrow materials throws pills, throwing head speed is 1850-2000 revolutions per minute, and when broad materials throws pills, throwing head speed is 1600-1700 revolutions per minute, (2) rolling overall pressure rate of a cold rolling being equals to or over 65%, (3) starting a first upper grinding head, a second upper grinding head and a third grinding head in the grinding time, firstly, the grain size of a abrasive band is polished, the new abrasive band is firstly ground to be attenuated on other steel coils, an abrasive band of the attenuation equal to or over 100 minutes and an abrasive band of the attenuation equals to or over 200 minutes, secondly, the abrasive band of the attenuation which equals to or over 100 minutes is mounted on the first upper grinding head, and then two abrasive bands of the attenuation equal to or over 200 minutes are installed on the second upper grinding head and the third grinding head to be precisely ground. The grinding method improves the surface quality of the frosted plate of the cold rolling and reduces the surface defects of the steel plate.

Description

technical field [0001] The invention relates to a grinding method for the surface of a high-grade stainless steel frosted plate. Background technique [0002] Stainless steel frosted plates are mainly used in products, decoration, construction and other industries. Due to the particularity of their use, stainless steel frosted plates have very high requirements on the surface. After entering 2006, the export volume of frosted plates has continued to increase, while foreign frosted plates Users have stricter requirements on the surface quality of products, not only high-grade and defect-free surface quality, but also strict requirements on the length, depth and uniformity of the grinding wire. Frosted boards have a wide range of uses, and are often used in elevator decoration, architectural decoration, electrical products, kitchen equipment, decoration and decoration, etc. The different uses of the products determine different requirements for the surface, especially the dome...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B24C1/10B24B21/04
Inventor 穆景权李旭初曾桂山
Owner SHANXI TAIGANG STAINLESS STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com