High-strength highly-permeable concrete and method for making the same

A technology of high water permeability and concrete, applied in the direction of climate sustainability, sustainable waste treatment, solid waste management, etc., can solve the problem of low compressive strength of concrete and achieve the effect of reducing water accumulation

Inactive Publication Date: 2008-05-21
SHENGHONG GRP CO LTD
View PDF0 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the key problem is that this kind of concrete generally has the disadvantage of low compressive strength.
At present, the compressive strength of permeable concrete pavement bricks developed in China is generally 10-25MPa, which is still far from the minimum compressive strength (30MPa) stipulated by the national building materials industry standard concrete pavement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] Table 1 Concrete formula table

[0013] According to the proportions in Table 1, we carried out various implementations numbered 1 to 3, mainly changing the water-cement ratio, respectively using 20%, 25% and 30% of the water-cement ratio for experiments. At the same time, in order to explore the relationship between the particle size of aggregate particles and the strength of permeable concrete, three different aggregate proportions were used.

[0014] The specific production process is as follows: according to the mixing ratio, the cement slurry is prepared on site, then the aggregate (mixed ash material) is poured in and forced to stir for 3 minutes, and then the concrete is produced by the method of pressure molding with a medium 10×20mm mold. Then use 200×200mm brick making mould and Hunan Zoomlion 250 type brick making machine to make pedestrian floor tiles. After the floor tiles are formed, they are cured for 1 day at a temperature of 20 °C and a humidity...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention aims at providing a concrete high strength and permeability and a preparation method thereof. The invention adopts the following technical scheme: cement with high strength, a special building material additive and special forming method are used; Aeolian sands in desert or fly ashes produced during the power generation of power plants are used as raw materials to prepare the concrete with high permeability. The used raw materials of the invention respectively are: 40-50 grade of ordinary porland cement; gravels, Aeolian sands in desert and fly ashes with respective particle diameter of 10.0-13.0mm, 5.0-10.0mm and 2.5-5.0mm, the adding ratio of which is selected freely; NNO type water reducing agent and JM-SCA type strengthening agent. The concrete made through the method is provided with good permeability, and the compressive strength can reach to 35MPa above. Passage tiles made through the method can be used to pave roads to greatly reduce hydrops on the surface of the roads. In local areas, sewer pipes even can be reduced or do not have to be paved. For even a heavy rainstorm encountered in 100 years happens, rains can rapidly permeate in soils through the tiles successfully in five minutes, which can be changed into renewable underground water.

Description

technical field [0001] The invention relates to a building material, more specifically to a high-strength, high-permeability concrete and a method for making pedestrian floor tiles, which belong to the field of new building materials. Background technique [0002] my country is a country with a large population and an extreme shortage of natural water resources. With the rapid development of modern industry and agriculture, a large amount of groundwater is extracted, and the ground surface that supplements groundwater is increasingly covered by impermeable asphalt or cement concrete materials, which makes the decreasing water resources more and more depleted. If this situation continues, it will inevitably cause the subsidence of the ground surface, resulting in the deformation and destruction of ground structures, which will directly affect the living space of human beings. Moreover, the rainwater that falls on the impervious ground during the rainy season not only increas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B14/06C04B18/08
CPCY02W30/91Y02A40/22
Inventor 郑凤莲
Owner SHENGHONG GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap