A technology for aviation tires and adhesives, applied in the direction of adhesives, natural rubber adhesives, adhesive types, etc., to achieve the effects of high initial bond strength, safe use, and high bond retention rate

Active Publication Date: 2008-06-18
中国化工集团曙光橡胶工业研究设计院有限公司
View PDF0 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the deficiencies of the prior art, and provide a high bonding strength, the old carcass and the refurbished parts are firmly combined, and there will be no delamination, bulging or quality problems on the joint surface, especially it can be combined with nylon / Aramid composite cord carcass firmly bonded aircraft tire retreading adhesive formula

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1   Embodiment 2

[0020] Raw material name Embodiment 1 Embodiment 2 Embodiment 3

[0021] 1 # Smoked sheet glue 80 90 100

[0022] SBR 1500 20 10 5

[0023] Adhesion promoter AIR-101 2 2 2

[0024] Binder RS ​​and Binder RA 2.5 2.5 2.5

[0025] High wear-resistant carbon black N330 20 15 20

[0026] White carbon black Jcsil 150 or Ultrasil7000GR 10 8 8

[0027] Ketoamine antioxidant RD 2.5 2.5 2.5

[0028] Insoluble sulfur IS-60 or IS-90 2.0 2.2 2.5

[0029] Sulphenamide accelerator NOBS or NS or CZ 1.5 1.5 1.5

[0030] Zinc oxide 5 5 5

[0031] Stearic acid 1.5 1.5 1.5

[0032] The preparation process of the above-mentioned raw materials is the same. According to the proportion of raw materials, the mixed rubber is first made by mixing in an internal mixer, and then the mixed rubber is mixed with gasoline in a ratio of 1:2-5 to make an adhesive, and the adhesive is evenly sprayed by spraying. Spray on the filing surface of the old carcass, after drying, add the rubber compound and r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses a prescription of an adhesive used for an aircraft tire retreading. The adhesive considers caoutchouc as the main material and also contains the main auxiliary materials of styrene butadiene rubber, adhesion promoter, adhesive, high abrasion furnace black, high dispersion white carbon black, ketoamine age inhibitor, indiscerptible sulfur and sulfenamide accelerant. The main material and the main auxiliary materials are made into gross rubber according to certain weight portion ratio, and the gross rubber is mixed with gasoline by certain proportion to be made into the adhesive. The adhesive of the prescription has the advantage that the adhesive solves the problem of sticking an old tire body with a retreading component when the aircraft tire is retreaded, which ensures that the aircraft tire does not have the problem of the delamination of the glue material between the old tire body and the retreading component, bulging and other quality problems during the use course, and the tire is safe for using.

Description

Technical field: [0001] The present invention relates to a polymer compound, in particular to the formulation of an adhesive used for retreading of aviation tires. Background technique: [0002] Aviation tires are used under the conditions of high speed, high load, instantaneous large impact force and large deformation. The requirement for retreaded aviation tires is to have safety under high load and high speed. When retreading aviation tires, an adhesive should be sprayed on the surface of the old tire after grinding to bond the old carcass and the retreaded parts together. The adhesive strength currently used is not enough, delamination, bulging and other quality problems will occur between the old aviation tire carcass and the retreaded parts after retreading, which will affect flight safety, especially when it can be used with nylon / aramid composite cord skeleton materials The bonding adhesive is still blank, and the nylon / aramid composite cord is a new type of skeleto...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J107/00C09J11/00
Inventor 俞华英刘蓉
Owner 中国化工集团曙光橡胶工业研究设计院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka