Oil shale slag lightweight high-strength haydite and producing method thereof

A technology of kerogen shale and high-strength ceramsite, which is applied in the field of building materials, can solve problems such as the shortage of raw materials and the way to absorb industrial solid waste, and achieve a good effect of energy saving and heat preservation

Inactive Publication Date: 2008-07-09
吉林省建筑材料工业设计研究院
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] The purpose of the present invention is to provide a light-weight high-strength ceramsite from kerogen shale slag and its production method, so as to solve the problems of the shortage of raw materials in the ceramsite market and the way to absorb industrial solid waste.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oil shale slag lightweight high-strength haydite and producing method thereof
  • Oil shale slag lightweight high-strength haydite and producing method thereof
  • Oil shale slag lightweight high-strength haydite and producing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Get raw material by following proportioning by weight:

[0050]Oil shale slag 58% The chemical composition is shown in Table 1

[0051] Plasticized material 20% chemical composition see table 2

[0052] Gas-generating material 20% The chemical composition is shown in Table 3

[0053] Stable gas-generating material 2% See Table 4 for chemical composition

[0054] The chemical composition of above-mentioned raw material is as follows:

[0055] Table 1 Chemical composition of kerogen shale slag in Huadian demonstration power plant

[0056]

[0057] Table 2 Chemical composition of Nong'an plasticized materials

[0058]

[0059] Table 3 Chemical composition of gas-generating materials in Xitai Township, Huadian

[0060]

[0061] Table 4 Chemical composition of stable gas-generating materials

[0062]

[0063] Mix the raw materials according to the above ratio, and add the ball mill to prepare the grinding material after mixing evenly; add a certain amount o...

Embodiment 2

[0065] Get raw material by following proportioning by weight:

[0066] See Table 1 for the chemical composition of kerosene shale residue 48%

[0067] Plasticized material 25% The chemical composition is shown in Table 2

[0068] Gas-generating material 25% The chemical composition is shown in Table 3

[0069] Stable gas-generating material 2% See Table 4 for chemical composition

[0070] Raw material chemical composition and manufacturing method are the same as embodiment 1, kiln temperature is controlled below 1250 ℃,

[0071] The bulk density of ceramsite is 600~800kg / m 3 .

Embodiment 3

[0073] Get raw material by following proportioning by weight:

[0074] Oil shale slag 52% The chemical composition is shown in Table 1

[0075] Plasticized material 23% Chemical composition see Table 2

[0076] Gas-generating material 23% See Table 3 for chemical composition

[0077] Stable gas-generating material 2% See Table 4 for chemical composition

[0078] The chemical composition and manufacturing method of raw materials are the same as in Example 1, the kiln temperature is controlled below 1250°C, and the bulk density of ceramsite is 600-800kg / m 3 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to oil shale slag haydites with light mass and high strength and the production method thereof, which belongs to constructional material. The invention is composed of oil shale slag, gas evolution materials, plasticizing materials and stable gas evolution materials according to the ratio of weight parts, grinding with materials, stirring with pre-watering, granulating by granulator after even agitation, then being sent into rotating kiln with double cylinders by belt conveyer for preheating, drying, roasting and cooling, the rotating kiln with double cylinders takes coal powders as the fuel, spraying the coal powders into the rotating kiln with double cylinders according to the speed and the dosage via speed variable motor driving screw conveyer and fan, controlling the preheating temperature between 450-850 DEC G and the calcination temperature between 1150-1250 DEC G. The invention has the advantages that utilizing the discarded oil shale slag to produce the haydite is an innovation. Further, the invention not only changes waste into valuable, but also is environment-friendly and has distinctive economic benefit and social benefit.

Description

technical field [0001] The invention relates to building materials, in particular to a light-weight high-strength ceramsite from kerogen shale slag and a production method thereof, especially to an ellipsoidal kerogen shale slag light-weight high-strength ceramsite prepared from kerogen shale slag as a raw material and a production method thereof. Background technique [0002] As we all know, with the development of the national economy, people's living standards continue to improve, the construction industry is developing rapidly, and the demand for new building materials in the construction industry is more urgent. Ceramsite is a kind of artificial concrete lightweight aggregate. Compared with natural aggregates such as gravel and river pebbles, it has a lower density, a honeycomb structure inside, and a closed and hard shell on the outside; the structure of ceramsite The characteristics make it low in density, and it also has high strength while maintaining heat insulation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132C04B33/32C04B38/02
CPCY02P40/60
Inventor 陈宇腾张明华黄旭光王玉萍李云飞钱红宇李泽林李升宇李巍巍邓家平刘冰洁
Owner 吉林省建筑材料工业设计研究院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com