Magnesium alloy microbial corrosion method based on solid medium

A solid culture medium, microbial corrosion technology, applied in biochemical equipment and methods, microbial determination/inspection, weather resistance/light resistance/corrosion resistance, etc. Intuitive results, saving experimental drugs, and the effect of saving experimental drugs

Inactive Publication Date: 2011-02-09
JILIN UNIV
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when studying the microbial corrosion of magnesium alloys in a liquid medium, it is difficult to complete the in-situ observation of microbial corrosion due to the fast diffusion of ions in the liquid medium

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnesium alloy microbial corrosion method based on solid medium
  • Magnesium alloy microbial corrosion method based on solid medium
  • Magnesium alloy microbial corrosion method based on solid medium

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0051] The microcorrosion research of AZ91 magnesium alloy carried out by using this method found that the main feature of microbiological corrosion of AZ91 magnesium alloy is pitting corrosion. image 3 . Through the sterile and sterile ( figure 2 and image 3 ) in the case of 24h corrosion morphology comparison. Prove that bacteria can indeed cause pitting corrosion of AZ91 magnesium alloy. The morphology of pitting is similar to that of bacterial colonies. pass image 3 It can be seen that the metabolism of bacterial colonies is particularly serious for the corrosion of magnesium alloys. Under the scanning electron microscope, the relationship between the position of the bacterial colony and the position of the corrosion pit in the corrosion morphology obtained by the patch corrosion method can be clearly observed. It can be deduced that the metabolism of the bacterial colony has an important influence on the corrosion pit. Figure 4 Polarization curves measured afte...

example 2

[0053] The effect of β phase content on the microbial corrosion of Mg-Al-Zn alloys was studied through the microbiological corrosion of AZ31, AZ51 and AZ71 magnesium alloys by chip corrosion method. in Figure 5 It is the corrosion morphology of AZ31 magnesium alloy in the presence of sulfate reducing bacteria for 24 hours. from Figure 5 It can be seen from the figure that the surface of the AZ31 magnesium alloy electrode has been severely corroded, especially the α phase, and the corrosion product film has cracked and formed larger plates. It can be concluded from the morphology that a thick corrosion product film has formed on the surface of the electrode. At the same time, a white substance is attached to the surface of the alpha phase, and the existence of bacterial cells can be clearly seen in the white substance. The white film layer is the reaction product of bacterial metabolites and magnesium alloy electrodes. Figure 6 Corrosion morphology of AZ51 magnesium allo...

example 3

[0056] Figure 9 and Figure 10 Shown are the topographic micrographs of the microbial corrosion of the Ce-modified AZ91 magnesium alloy. The picture shows the corrosion morphology of the Ce-modified AZ91 magnesium alloy at 24 h when sterile. Figure 10 Microbial corrosion morphology of Ce-modified AZ91 magnesium alloy at 24h. from Figure 10 As can be seen, the distribution of bacteria and the way they divide. pass Figure 9 and Figure 10 By comparison, the influence of the presence of sulfate-reducing bacteria and their metabolism on the corrosion process of Ce-modified AZ91 magnesium alloy can be obtained.

[0057] Therefore, it can be seen from the above examples that the patch corrosion method is an effective research method for the study of microbial corrosion of magnesium alloys.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a sulfate reducing bacteria microbe corrosion method of magnesium alloy, for resolving the microbe corrosion problem of magnesium alloy and combining the microbe cultivation technique and microbe corrosion technique of solid culture medium to provide a novel magnesium alloy microbe corrosion method based on solid culture medium. The method comprises (1) processing and disinfecting sample, (2) arranging and disinfecting a solid culture medium, (3) cultivating and activating bacterial, (4) corroding paster. The invention optimizes the components of electrolyte to highlight the bacterial performance in the corrosion process of magnesium alloy, and compares the electrode surface corrosion morphology with bacterial and without bacterial, to provide the reference for magnesium alloy microbe corrosion mechanism research. The inventive method is suitable for magnesium alloy microbe corrosion research.

Description

Technical field: [0001] The invention relates to a sulfate-reducing bacteria microbial corrosion method for magnesium alloys, in particular to a solid medium-based magnesium alloy microbial corrosion method. The method adopts the patch corrosion method, which is mainly used as a method for microbial corrosion of magnesium alloy components in humid environments where sulfate-reducing bacteria may exist and in environments where organic substances exist. Background technique: [0002] The phenomena that are caused by the life activities of microorganisms or promote the corrosion of materials are collectively referred to as microbial corrosion (MIC). Any facility in contact with water, soil or humid air may encounter microbial corrosion. Power plant cooling water circulation system, heat exchange system, oil extraction, storage and transportation system, sewage treatment pipeline, drinking water pipeline, aircraft fuel storage tank, paper mill equipment, metal cutting fluid ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N17/02C12Q1/02
Inventor 刘耀辉王强宋雨来
Owner JILIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com