Bamboo compound material wind mill blade and its vacuum infusion process

A technology of wind turbine blades and composite materials, which is applied to wind turbines, wind turbine components, and wind turbines in the same direction as the wind. It can solve the problems of long production cycle, large manpower and material resources, and increased costs, and achieve manufacturing costs. Low cost, good for environmental protection, and short production cycle

Inactive Publication Date: 2008-08-06
无锡天奇竹风科技有限公司
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, most of the blades used in wind power generation equipment in the world use FRP as the main structure, but for blades with a length of more than 30 meters, it is usually necessary to add expensive carbon fiber to make up for the lack of material stiffness, which undoubtedly increases production. The cost of manufacturing,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bamboo compound material wind mill blade and its vacuum infusion process
  • Bamboo compound material wind mill blade and its vacuum infusion process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Step 1: Prepare the root preform of the blade body

[0043] 1a. According to the shape and size of the larger part of the blade root curvature, divide it into several pieces to make a mold for the preformed part of the blade root, remove the sundries on the surface of the mold, and wipe the surface of the mold with a mold cleaner and a mold release agent in turn, Adhesive sealing tape around the flange edge of the mold of the blade root preformed part;

[0044] 1b, lay release cloth on the mold of step 1a, lay multiple layers of bamboo sheets closely side by side on the release cloth, lay release cloth on the bamboo sheet layer again to form bamboo laying layer, lay bamboo laying Arrange infusion matrix material pipelines and diversion nets on the top of the layer;

[0045] 1c. Bond the vacuum bag and the mold with sealing tape, place the layer formed by the bamboo layer, release cloth and diversion net in a closed space, and pump air into the vacuum bag to make the pr...

Embodiment 2

[0063] Step 1: Prepare the root preform of the blade body

[0064] 1a. According to the shape and size of the blade root, make a mold for the preformed part of the blade root, remove the impurities on the surface of the mold, wipe the surface of the mold with a mold cleaner and a mold release agent in turn, and clean the flange of the mold for the preformed part of the blade root. Adhesive sealing tape around the edge;

[0065] 1b, lay release cloth on the mold of step 1a, lay multiple layers of bamboo sheets closely side by side on the release cloth, lay release cloth on the bamboo sheet layer again to form bamboo laying layer, lay bamboo laying Arrange infusion matrix material pipelines and diversion nets on the top of the layer;

[0066] 1c. Bond the vacuum bag and the mold with sealing tape, place the layer formed by the bamboo layer, release cloth and diversion net in a closed space, and pump air into the vacuum bag to make the pressure in the vacuum bag -0.6atm;

[00...

Embodiment 3

[0084] Step 1: Prepare the root preform of the blade body

[0085] 1a. According to the shape and size of the larger part of the blade root curvature, divide it into several pieces to make a mold for the preformed part of the blade root, remove the sundries on the surface of the mold, and wipe the surface of the mold with a mold cleaner and a mold release agent in turn, Adhesive sealing tape around the flange edge of the mold of the blade root preformed part;

[0086] 1b, lay release cloth on the mold of step 1a, lay multiple layers of bamboo sheets closely side by side on the release cloth, lay release cloth on the bamboo sheet layer again to form bamboo laying layer, lay bamboo laying Arrange infusion matrix material pipelines and diversion nets on the top of the layer;

[0087] 1c. Bond the vacuum bag and the mold with sealing tape, place the layer formed by the bamboo layer, release cloth and diversion net in a closed space, and pump air into the vacuum bag to make the pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a bamboo-made composite material wind power vane and a vacuum infusion technique. According to the technique scheme provided by the invention, the bamboo-made composite material wind power vane comprises a vane body which is composed of a vane-shaped upper vane and lower vane, wherein the vane root is arranged at the root part of the vane body, the top end of the vane body is a vane tip, the upper and the lower vanes are adhered into an integral by mold adhesive bar and makes the periphery form a cavity, a bamboo cordwood is filled in the vane root and/or upper vane and/or lower vane, a vane root premolding part is arranged on the bottom end corner of the vane outer-boundary of the vane body. The vane is prepared by each procedure such as preparing equipment material, preparing mould, paving each kind of material, laying out tube, infusing, doing subsequent process and the like. The vane is low in preparation cost, short in preparation period, which is beneficial to protect environment, easy to control the preparation procedure and obtain raw materials.

Description

technical field [0001] The invention discloses a wind turbine blade made of bamboo composite material and a vacuum infusion process of the wind turbine blade made of bamboo composite material. Background technique [0002] At present, most of the blades used in wind power generation equipment in the world use FRP as the main structure, but for blades longer than 30 meters, it is usually necessary to add expensive carbon fiber to make up for the lack of material stiffness, which undoubtedly increases production. The cost of manufacturing, the production cycle is long, and the waste products in the manufacturing process of the blades and the damaged products after use are not easy to recycle. Random discarding will definitely cause environmental pollution, making it costly to dispose of these waste products and damaged products reasonably human and material resources. Contents of the invention [0003] The object of the present invention is to overcome the deficiencies in t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): F03D1/06F03D11/00B29D31/00B29C70/34B29C70/54B29C65/00B29K311/14B29K309/08B29D99/00
CPCY02E10/72Y02E10/728Y02P70/50
Inventor 齐海宁王鹏飞董雷
Owner 无锡天奇竹风科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap