Positive photoresist composition, thick film photoresist laminate, method for producing thick film resist pattern, and method for producing connecting terminal

A photoresist layer, photoresist technology, applied in photosensitive materials for photomechanical devices, use/removal methods of circuit masks, photomechanical devices, etc., can solve the problem of not being able to obtain high precision Resist patterns, etc.

Inactive Publication Date: 2008-08-20
TOKYO OHKA KOGYO CO LTD
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, when a photoresist layer is formed on a substrate containing copper using a chemically amplified photoresist composition, there arises a problem that high precision cannot be obtained due to an adverse effect exerted by copper. resist pattern

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Positive photoresist composition, thick film photoresist laminate, method for producing thick film resist pattern, and method for producing connecting terminal
  • Positive photoresist composition, thick film photoresist laminate, method for producing thick film resist pattern, and method for producing connecting terminal
  • Positive photoresist composition, thick film photoresist laminate, method for producing thick film resist pattern, and method for producing connecting terminal

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0256] [Synthesis Example 1]

[0257] After replacing the atmosphere in the flask equipped with a stirrer, a reflux condenser, a thermometer, and a dropping tank, propylene glycol methyl ether acetate was charged as a solvent, and stirring was started. Then, the temperature of the solvent was raised to 80°C. 2,2'-Azobisisobutyronitrile as a polymerization catalyst, 30 mol% of 2-methoxyethyl acrylate constituting units, 10 mol% of n-butyl acrylate constituting unit, 55 mol% of 2-ethyl-2-adamantyl methacrylate constituting unit represented by the following chemical formula, and 5 mol% of acrylic acid constituting unit, followed by stirring until the polymerization catalyst was dissolved. This solution was uniformly added dropwise to the flask over 3 hours, followed by polymerization at 80°C for 5 hours. The reaction product was cooled to room temperature, and then classified to obtain a resin (B-1) having a mass average molecular weight of 30,000.

Embodiment 2

[0258] [Synthesis Example 2]

[0259] In addition to using 30 mol% of 2-methoxyethyl acrylate constituting unit, 10 mol% of n-butyl acrylic acid constituting unit, 55 mol% of 2-ethyl-2-adamantyl methacrylate constituting unit represented by the following chemical formula In the same manner as in Synthesis Example 1 except for 5 mol% of acrylic acid constituting units as constituting units, a resin (B-2) having a mass average molecular weight of 100,000 was obtained.

[0260] [chemical formula 27]

[0261]

Embodiment 3

[0263]

[0264] Resin (C-1) having a mass average molecular weight of 1,500 was obtained in the same manner as in Synthesis Example 1 except that 10 mol% of hydroxystyrene constituting units and 90 mol% of styrene constituting units were used as constituting units.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
dispersityaaaaaaaaaa
Login to view more

Abstract

This positive photoresist composition is a positive photoresist composition for exposing to light having one or more wavelengths selected from g-rays, h-rays and i-rays, comprising: (A) a compound which generates an acid under irradiation with active rays or radiation, and (B) a resin whose solubility in an alkali is enhanced by an action of an acid, wherein the component (A) contains an onium salt (A1) having a naphthalene ring in the cation moiety.

Description

technical field [0001] The present invention relates to a positive photoresist composition, a thick film photoresist laminate, a method for preparing a thick film resist pattern and a method for preparing a connection terminal. [0002] This application claims priority from Japanese Patent Application No. 2005-099442 filed on March 30, 2005, the disclosure of which is incorporated herein by reference. Background technique [0003] With recent miniaturization of electronic devices, there is rapid progress toward higher integration of LSIs. In order to mount an LSI on an electronic device, a multipin film packaging method in which a connection terminal constituted by protruding electrodes is placed on a support such as a substrate is used. In this multi-pin packaging method, a terminal composed of a bump protruding from a support and a terminal comprising a post called a metal post protruding from the support and solder balls formed thereon are used. [0004] The bumps or me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G03F7/004G03F7/039H01L21/60
CPCG03F7/0397H01L21/4853G03F7/0045H01L24/13H01L2224/1146H01L2924/01019H01L2224/13144H01L2924/01029H01L2224/13147H01L2224/1147H01L24/11H01L2924/01013H01L2924/014H05K3/0076H01L2924/01024H01L2924/01079H01L2224/13155H05K3/0079H01L2924/01033H01L2924/01005H01L2924/01006H01L2224/81192H05K3/3452H01L2924/01074H01L2924/01078H01L2924/01057H01L2924/01073H01L2224/131H01L2924/3025H01L2924/15747H01L2924/15788H01L2924/00014H01L2924/00G03F7/0047G03F7/0392
Inventor 三隅浩一鹫尾泰史先崎尊博斋藤宏二
Owner TOKYO OHKA KOGYO CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap