Lemon acid gold salt for gold plating and manufacture method thereof

A gold citrate and citric acid technology, applied in the chemical field, can solve the problems of high potassium cyanide content, high toxicity, and limited use, and achieve the effect of reducing wastewater treatment costs and pollution

Inactive Publication Date: 2008-08-27
HENGSHENG TECH R&D CO LTD
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In alkaline cyanide gold plating, the auxiliary materials are potassium cyanide, potassium carbonate, and potassium dihydrogen phosphate. Because the conten

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lemon acid gold salt for gold plating and manufacture method thereof
  • Lemon acid gold salt for gold plating and manufacture method thereof
  • Lemon acid gold salt for gold plating and manufacture method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The molecular formula of auramine citrate for gold plating is: K 3 Au 2 C 9 h 5 o 7 N 2 , the structural formula is:

[0017]

[0018] Calculated by preparing 1000g of citrate gold salt.

[0019] Example 1, at normal temperature and pressure, add 10000mL of water into the reactor, turn on the stirrer and heating switch, and when the temperature of the water rises to 85°C, add 500g of gold trichloride under stirring conditions to make it completely dissolve With the above-mentioned gold trichloride solution under stirring conditions, keep the temperature at 85°C, concentrate for 4 hours, when the volume is 2000mL, add water to the reactor to 10000mL, and then concentrate to 2000mL under the same conditions, Add water to 10000mL; keep the above-mentioned gold trichloride solution at 85°C, take 800g of potassium citrate, dissolve it in 20000mL of 85°C hot water, filter to remove trace impurities in the solution, and add the prepared potassium citrate solution to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses citric acid gold salt used for plating gold and a method for preparing the citric acid gold salt, the molecular formula of the citric acid gold salt is K3Au2C9H5O7N2, and the method comprises the following steps: dissolving gold trichloride in water with certain temperature, then concentrating and diluting the gold trichloride time after time under the temperature, and preparing and obtaining organometallic salt through reacting with potassium citrate, EDTA and thiocyanate amine in certain temperature and time in a catalyst case. The citric acid gold salt has the advantages that the toxicity is low, the discharge liquid after the gold plating only contains trace quantity free CN-, the cost of treating waste water of electroplating enterprises is reduced, and the pollution to environment of discharging of cyanide is originally reduced.

Description

technical field [0001] The invention relates to a gold salt for gold plating, in particular to a gold citrate salt for gold plating, and also relates to a preparation method of the gold citrate salt, which belongs to the technical field of chemistry. Background technique [0002] In the gold plating industry, due to the strong complexing force of potassium cyanide on gold ions, most enterprises in my country choose the inorganic electroplating gold salt—potassium gold cyanide as the main salt of gold plating during electroplating. According to the corrosion resistance and the characteristics of the coating and the plated parts, the acid gold plating or alkaline gold plating solution is prepared to meet the requirements of the process conditions. [0003] National Defense Industry Press published the first edition in June 1990, and the book "Practical Electroplating Process" edited by Li Hongnian, Zhang Shaogong, Zhang Bingqian, Song Ziyu, etc., which was printed for the secon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C25D3/48
Inventor 张群刚
Owner HENGSHENG TECH R&D CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products