Method for preparing meso-porous nano hydroxyl phosphorite crystal
A nano-hydroxyapatite and crystal technology, applied in chemical instruments and methods, prostheses, phosphorus compounds, etc., can solve the problems of low mechanical strength, poor regularity of material structure, restricting application, etc., and achieve large specific surface area, high biological Activity and biocompatibility, effect of perfect crystal development
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0013] The present invention is a kind of preparation method of mesoporous nano-hydroxyapatite crystal, and its steps are:
[0014] (1) Take a certain amount of soluble calcium salt and phosphorus pentoxide or phosphoric acid ester by weighing the stoichiometric ratio of Ca / P=1.67;
[0015] (2) dissolving phosphorus pentoxide or phosphoric acid ester in the alcoholic solution, dissolving the soluble calcium salt in the aqueous solution, the volume ratio of the aqueous solution to the alcoholic solution is 2 / 3, or 1, or 3 / 2;
[0016] (3) Mix the above two solutions, adjust the pH value of the mixed solution between 9 and 10 with ammonia water, and stir fully;
[0017] (4) Pour the above solution into a reaction kettle, and carry out a hydrothermal reaction at a temperature of 140° C. to 180° C. for 8 hours to obtain hydroxyapatite precipitation;
[0018] (5) The precipitate was washed with distilled water, filtered with suction, and dried at 200° C. to obtain mesoporous nano-h...
Embodiment 1
[0022] Take a certain amount of calcium nitrate tetrahydrate (Ca(NO) by weighing the stoichiometric ratio of Ca / P=1.67 3 ) 2 4H 2 O) and phosphorus pentoxide (P 2 o 5 ), be dissolved in distilled water and ethanol solution respectively, the volume ratio of aqueous solution and ethanol solution is 2 / 3, adopt ultrasonic shock to dissolve, above-mentioned solution is mixed, adopt magnetic stirrer to stir, pH value is adjusted at 9 with ammonia water, then The above mixed solution was poured into a reaction kettle, hydrothermally reacted at a temperature of 140°C for 8 hours, the precipitate was repeatedly washed with distilled water, suction filtered, and dried at 200°C to obtain mesoporous nano-hydroxyapatite crystals.
[0023] X-ray diffraction results show that the obtained product is a hydroxyapatite crystal with higher purity, and almost no other impurity phases exist; as figure 1 As shown, the nano-hydroxyapatite crystal has a mesoporous structure, the particle size is ...
Embodiment 2
[0025] Weigh a certain amount of Ca(NO) according to the stoichiometric ratio of Ca / P=1.67 3 ) 2 4H 2 O and P 2 o 5 , respectively dissolved in distilled water and propanol solution, the volume ratio of the aqueous solution to the propanol solution is 1, ultrasonically oscillated to dissolve, mix the above solutions, stir with a magnetic stirrer, adjust the pH value to 10 with ammonia water, and then mix the above The solution was poured into a reaction kettle, subjected to hydrothermal reaction at a temperature of 160° C. for 8 hours, the precipitate was repeatedly washed with distilled water, filtered with suction, and dried at 200° C. to obtain mesoporous nano-hydroxyapatite crystals. The result is basically the same as Example 1.
PUM
Property | Measurement | Unit |
---|---|---|
pore size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com