Preparation of high-strength environment-friendly skin gelatin
A skin gelatin, high-strength technology, applied in the direction of protein waste adhesives, rosin coatings, etc., can solve the problems of affecting the fluidity of the rubber material, viscosity increase, etc., and achieve fast drying speed, short synthesis time, and high bonding strength Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0006] Embodiment 1: at first by the mass ratio of 1: 3, skin gelatin and water are jointly added in the reactor, be warmed up to 75, 85, 80, 78, 82 ℃, then add the concentration of 6g by every 100g glue solution and be 6mol / L of hydrochloric acid, reacted for 0.5h, cooled to 45°C to form glue, then added 3ml of epichlorohydrin per 100g of glue, reacted at 45°C for 1.3h, and obtained modified skin gelatin; followed by 1:8 The mass ratio of caustic soda is dissolved in water, and heated to boiling to completely dissolve the caustic soda to form a caustic soda solution, then slowly add rosin of the same quality as the caustic soda solution, and stir while adding, until the rosin is completely dissolved and becomes amber viscous After the reaction ends, the modified rosin is obtained, and water with 5 times the quality of the caustic soda solution is added to obtain a modified rosin emulsion; the modified gelatin and the modified rosin emulsion are stirred at room temperature in ...
Embodiment 2
[0007] Embodiment 2: first by the mass ratio of 1: 3.5, hide gelatin and water are jointly added in the reactor, be warmed up to 80 ℃, then add the hydrochloric acid that the concentration of 7g is 6mol / L by every 100g glue solution, react 0.8h, Cool down to 42°C to form glue, then add 4ml of epichlorohydrin per 100g of glue, react at 42°C for 1 hour to obtain modified skin gelatin; then dissolve caustic soda in water at a mass ratio of 1:10, And heated to boiling to completely dissolve the caustic soda to make a caustic soda solution, then slowly add rosin of the same quality as the caustic soda solution, and assist in stirring while adding, until the rosin is completely dissolved into an amber viscous liquid, the reaction is completed, and the modified Rosin, then add water with 4 times the mass of caustic soda solution to obtain a modified rosin emulsion; take the modified gelatin and the modified rosin emulsion at room temperature and stir them evenly at a mass ratio of 6:1...
Embodiment 3
[0008] Embodiment 3: at first by the mass ratio of 1: 4, skin gelatin and water are jointly added in the reactor, be warmed up to 80 ℃, then add the hydrochloric acid that the concentration of 8g is 6mol / L by every 100g glue solution, react 0.6h, Cool down to 40°C to form glue, then add 2.5ml of epichlorohydrin per 100g of glue, react at 40°C for 1.5h to obtain modified skin gelatin; then dissolve caustic soda in water, and heated to boiling to completely dissolve the caustic soda to make a caustic soda solution, then slowly add rosin with the same quality as the caustic soda solution, and assist in stirring while adding, until the rosin is completely dissolved into an amber viscous liquid, and the reaction is completed. Modified rosin, then add water with 4.5 times the quality of caustic soda solution to obtain modified rosin emulsion; get modified skin gelatin and modified rosin emulsion at room temperature and stir at a mass ratio of 5.2:1 to obtain a mixed glue, and then pr...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap