Nickel-metal hydride battery

一种镍氢蓄电池、电解液的技术，应用在镍蓄电池、碱性蓄电池、碱性蓄电池电极等方向，能够解决不能充分地抑制自放电等问题，达到抑制自放电、减少电力消耗、有利于环境的效果

Active Publication Date: 2012-01-18
FDK CORP
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, self-discharge cannot be sufficiently suppressed even if the separator of said publication is used in a nickel metal hydride storage battery

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nickel-metal hydride battery
  • Nickel-metal hydride battery
  • Nickel-metal hydride battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] 1. Fabrication of Negative Plate

[0041] The weighing composition is La 0.10 Ce 0.05 PR 0.35 Nd 0.50 Mg 0.10 Ni 3.70 Al 0.22 The metal raw materials are mixed, and the mixture is melted in a high-frequency melting furnace to obtain an ingot. The ingot was heated in an argon atmosphere at a temperature of 1000°C for 10 hours, so that the crystal structure in the ingot became Ce 2 Ni 7type structure or similar structure. Afterwards, the ingot is mechanically pulverized and screened in an inactive environment to obtain rare earth Mg—Ni hydrogen storage alloy particles having the above composition. In addition, the average particle size of the obtained rare earth Mg—Ni-based hydrogen storage alloy was 50 μm. The average particle size is the particle size at which the weight integral reaches 50% in the particle size distribution of the rare earth Mg—Ni-based hydrogen storage alloy measured using a laser diffraction / scattering type particle size distribution measur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

A positive electrode plate (3) of a nickel-metal hydride battery contains nickel hydroxide particles (18), a coating layer (19) covering at least a part of the surface of each nickel hydroxide particle (18) and mainly composed of a cobalt compound having an average valence of cobalt more than 2, and additives (15, 16) respectively containing Nb and Y and distributed among the nickel hydroxide particles (18). A negative electrode plate (4) contains a hydrogen storage alloy having a Co content of not more than 2.0% by mass, and a separator (5) contains a fiber having a sulfone group. An alkaline electrolyte solution contains sodium hydroxide as the main solute.

Description

technical field [0001] The present invention relates to nickel metal hydride storage battery. Background technique [0002] Ni-MH storage batteries are widely used due to their high capacity characteristics. However, nickel-metal hydride batteries tend to reduce the remaining capacity through self-discharge, and when they are used again after a period of time after charging, they need to be recharged. [0003] In order to improve the problems caused by this self-discharge, for example, in the nickel-metal hydride storage battery disclosed in the Japanese Patent Laid-Open No. 62-115657, a non-woven fabric made of sulfonated polyolefin resin is used as a separator . [0004] However, self-discharge cannot be sufficiently suppressed even if the separator of the above-mentioned publication is used in a nickel-metal hydride storage battery. Contents of the invention [0005] An object of the present invention is to provide a nickel-hydrogen storage battery capable of supp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M10/30H01M2/16H01M4/32H01M4/38H01M4/52H01M4/62C22C19/00
CPCH01M2004/027Y02E60/124H01M4/32H01M4/383H01M2004/028H01M2/1606H01M4/52H01M10/345H01M4/242H01M4/362Y02E60/10H01M50/44H01M10/30H01M4/62H01M10/26
Inventor 泉康士前田泰史
Owner FDK CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com