A low temperature resistant long-life lithium-ion battery

A lithium-ion battery and low-temperature-resistant technology, which is applied in the manufacture of battery electrodes, secondary batteries, and electrolyte batteries, can solve problems such as low energy density, short cycle life, and poor charge-discharge performance, and achieve good compatibility and high Low temperature cycle performance, excellent performance effect

Active Publication Date: 2020-09-11
北京北方华创新能源锂电装备技术有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide a long-life lithium ion battery with low temperature resistance, which overcomes the problems of poor charge and discharge performance, short cycle life and low energy density of existing lithium ion batteries at low temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A low temperature resistant long-life lithium-ion battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Example 1: LiNi with D50 of 8 μm is selected 0.5 co 0.2 mn 0.3 o 3 (hereinafter referred to as NCM523) as the cathode material. First mix the positive electrode material NCM523 and the conductive agent acetylene black (hereinafter referred to as HS-100), then add the binder PVDF and the solvent N-methylpyrrolidone (hereinafter referred to as NMP), and stir to prepare the positive electrode slurry. The distribution ratio of positive electrode material, conductive agent and binder is in accordance with NCM523:HS-100:PVDF=95:3:2. The slurry is coated, rolled, cut and dried to obtain a positive electrode sheet.

[0028] Modified natural graphite was selected as the negative electrode material. First mix natural graphite C, conductive agent carbon black (hereinafter referred to as SPC), and carboxymethyl cellulose (hereinafter referred to as CMC), then add solvent water and styrene-butadiene rubber (hereinafter referred to as SBR), and stir to prepare negative electrode...

Embodiment 2

[0030] Example 2: NCM523 with a D50 of 8 μm is selected as the positive electrode material. First mix the positive electrode material NCM523 and the conductive agent HS-100, then add the binder PVDF and the solvent NMP, and stir to prepare the positive electrode slurry. The distribution ratio of each component is in accordance with NCM523:HS-100:PVDF=94:3:3. The slurry is coated, rolled, cut and dried to obtain a positive electrode sheet.

[0031] Modified natural graphite was selected as the negative electrode material. First mix natural graphite C, conductive agent SPC, and CMC, then add solvent water and SBR, and stir to prepare negative electrode slurry. The distribution ratio of each component is in accordance with C:SPC:CMC:SBR=95:2:1:2. The slurry is coated, rolled, cut and dried to obtain a negative electrode sheet.

[0032] The positive electrode sheet, the negative electrode sheet, and the diaphragm are wound and hot pressed to obtain a core. The battery is inje...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-temperature-resistant long-life lithium ion battery. The positive electrode active material of the lithium ion battery has a median diameter of 5.5 μm≤D50≤10 μm, the negative electrode is a modified graphite material, and a low-temperature additive is added to the electrolyte. The lithium-ion battery disclosed by the present invention has excellent low-temperature charging and discharging performance, and has a long cycle life at low temperature. The lithium-ion battery can be used as an energy storage battery and a battery for electric vehicles in a low-temperature environment.

Description

technical field [0001] The invention relates to the technical field of batteries, in particular to a low-temperature-resistant and long-life lithium-ion battery. Background technique [0002] In the era of new energy, lithium-ion batteries have been widely used. People have higher requirements for the charging and discharging performance of lithium-ion batteries in low-temperature environments. They hope that they can be used in northern cold regions or in the wild, and can be used in power vehicles or energy storage fields. However, the current research on the low-temperature characteristics of lithium-ion batteries is obviously lagging behind. When the ambient temperature is lower than 0°C, the performance of the battery will decline significantly or it will not work normally. . Therefore, it is of great significance to develop long-life Li-ion batteries that are resistant to low temperatures. [0003] For most systems, the decrease of charge transfer rate and lithium io...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/505H01M4/525H01M4/587H01M10/0525H01M10/0567H01M10/058
CPCH01M4/364H01M4/505H01M4/525H01M4/587H01M10/0525H01M10/0567H01M10/058H01M2300/0037Y02E60/10Y02P70/50
Inventor 丁莹刘晓晔杨映华
Owner 北京北方华创新能源锂电装备技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com