Deflection-proof friction disk of ultrahigh molecular weight polyethylene material and preparation method thereof

A technology of ultra-high molecular weight and polyethylene, applied in the field of ultra-high molecular weight polyethylene material anti-bias friction disc and its preparation, can solve the problem of affecting the normal operation and conveying efficiency of the conveyor, the high production cost of the anti-bias friction disc, and no corrosion resistance To achieve excellent comprehensive performance, highlight substantive features, and prolong service life

Inactive Publication Date: 2008-12-10
王好占
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The anti-deflection friction disc of the steel friction self-aligning idler has high production cost, heavy weight, high energy consumption, no cor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] An ultra-high molecular weight polyethylene material anti-deflection friction disc for friction self-aligning idlers. In parts by weight, the ultra-high molecular weight polyethylene material used in the anti-deflection friction disc is composed of the following components: ultra-high molecular weight polyethylene 100 4 parts of polyethylene wax, 2 parts of graphite, 10 parts of glass hollow microspheres, 5 parts of flame retardant, 0.9 part of coupling agent, 0.3 part of nucleating agent, and 1.5 parts of antioxidant.

[0035] Based on the above, the ultra-high molecular weight polyethylene is ultra-high molecular weight polyethylene with a matrix viscosity-average molecular weight of 1.5 to 5 million.

[0036] Based on the above, the flame retardant is at least one of antimony trioxide, phosphoric acid ester, stannate and / or decabromodiphenyl ether.

[0037] Based on the above, the coupling agent is at least one of a silane coupling agent, a titanate coupling agent, a...

Embodiment 2

[0047] The difference between this embodiment and embodiment 1 mainly lies in:

[0048] An ultra-high molecular weight polyethylene material anti-deflection friction disc for friction self-aligning idlers. The ultra-high molecular weight polyethylene material used in the anti-deflection friction disc is composed of the following components: ultra-high molecular weight polyethylene 70 6 parts of polyethylene wax, 3 parts of graphite, 10 parts of glass hollow microspheres, 5.5 parts of flame retardant, 1.2 parts of coupling agent, 0.4 parts of nucleating agent, and 2.2 parts of antioxidant.

Embodiment 3

[0050] The difference between this embodiment and embodiment 1 mainly lies in:

[0051] An ultra-high molecular weight polyethylene material anti-deflection friction disc for friction self-aligning idlers. In parts by weight, the ultra-high molecular weight polyethylene material used in the anti-deflection friction disc is composed of the following components: ultra-high molecular weight polyethylene 150 4 parts of polyethylene wax, 2 parts of graphite, 12 parts of glass hollow microspheres, 6.5 parts of flame retardant, 1.5 parts of coupling agent, 0.5 parts of nucleating agent, and 3.2 parts of antioxidant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an anti-deviation friction disc made of an ultra-high molecular weight polyethylene material and a preparation method thereof. The ultra-high molecular weight polyethylene material used by the anti-deviation friction disc comprises the following compositions by weight portion: 50 to 150 portions of ultra-high molecular weight polyethylene, 2 to 6 portions of tissuemat E, 1 to 3 portions of graphite, 5 to 15 portions of glass hollow microbeads, 2.5 to 7.5 portions of a flame retardant, 0.3 to 1.9 portions of a coupling agent, 0.1 to 0.5 portions of a nucleating agent and 0.5 to 3.2 portions of an antioxidizer. The preparation method comprises the following steps of batching, mixing, heating, hydraulic pressing, cooling, demolding and forming. The material has high wearing resistance, good self-lubricity, super shock strength, good fire resistance, super inadhesion, age resistance and corrosion resistance, and is mainly applied to the manufacture of the friction aligning idler anti-deviation friction disc.

Description

technical field [0001] The invention relates to an ultra-high molecular weight polyethylene material anti-bias friction plate for friction self-aligning idlers and a preparation method thereof, belonging to the field of polymer processing applications. Background technique [0002] Rollers are widely used in open-air, dusty and highly corrosive harsh environments, such as mining industry, chemical industry, coking industry, steel industry, electric power industry, coal washing industry, grain processing industry, metallurgical industry, cement production industry, etc. The friction self-aligning idler roller can prevent the conveyor belt from being damaged and deviation, and it uses the friction resistance and the deviation adjustment mechanism of the friction wheel radian to prevent and correct the deviation of the conveyor belt. The anti-deflection friction disc of the steel friction self-aligning roller has high production cost, heavy weight, high energy consumption, no c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/06C08K3/04C08K7/28C08K13/04C08J5/14B29B7/00B29C43/02B29C43/52
Inventor 王好占
Owner 王好占
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap