A magnesium alloy and tailor-welded blank technology, applied in forming tools, metal processing equipment, manufacturing tools, etc., can solve problems such as low strength and rigidity of die-casting parts, unfavorable electronic shielding effect, difficult plastic forming processing, etc., to avoid cracking or The effect of weld offset, avoiding cracking or severe weld offset, and uniform deformation

Inactive Publication Date: 2009-03-11
SHENYANG LIGONG UNIV
View PDF1 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Disadvantages of die-casting method: low strength and rigidity of die-casting parts, low density (not conducive to electronic shielding effect)
However, magnesium alloys have poor plasticity at room temperature, are prone to brittle cracks, and are difficult to p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Deep drawing method of magnesium alloy tailor welded blanks
  • Deep drawing method of magnesium alloy tailor welded blanks
  • Deep drawing method of magnesium alloy tailor welded blanks

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] A magnesium alloy tailored welded blank drawing forming device according to the present invention comprises an upper template 1, a drawing punch fixing plate 2, a drawing punch 3, a blank holder 4, a blank 5, a drawing die 6, and a heating plate 7. The lower template 8, wherein the heating plate 7 is located below the drawing die 6, and a plurality of electric heating rods 9 are respectively inserted on the drawing die 6 and the blank holder 4. The device of the present invention has been disclosed and authorized, and the patent No. is ZL02144943.0, so the structure of the device is no longer described.

[0028] A method for deep drawing of magnesium alloy tailor welded blanks, comprising the following operations:

[0029] The deep drawing of AZ31 and AZ80 magnesium alloy tailored welded blanks is taken as an example to illustrate. Operation steps for deep drawing of AZ31 and AZ80 magnesium alloy tailored welded blanks:

[0030] 1) Blank preparation: the blank is weld...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a deepening and shaping method for a Mg-alloy tailor-welded blank which includes the following technique flows: 1) preparing a blank material: a lubricant is coated on the blank material of the Mg-alloy tailor-welded blank; 2) preheating a die: the die is heated to a preset temperature and the blank material is put in the die after the temperature detected by a thermoelectric couple reaches a preset value; the blank material is heated together with the die; 3) heating the blank material: after the blank material and the die are heated together for 5 to 10 minutes, deepening and shaping is prepared; 4) deepening and shaping: the deepening and shaping speed is controlled in a preset range and deepening and shaping is carried out; 5) finishing the deepening and shaping, after the deepening and shaping is finished, a workpiece is taken out. The method realizes the uniform deformation during the deepening and shaping process of the Mg-alloy tailor-welded blank, avoids the defects of cracking or serious deviation of a welding line and improves the product quality; a deepening and shaping device for the Mg-alloy tailor-welded blank can lead the blank material to realize grads temperature field distribution; besides, the temperature control method is simple which can realize different temperature grads fields only by changing the number and distribution of heating rods.

Description

technical field [0001] The patent of the invention relates to a method for deep-drawing of magnesium alloy tailor-welded blanks, and also a method for controlling the movement of weld seams during deep-drawing of magnesium alloy tailor-welded blanks, that is, using gradient temperature field to control the drawing deformation of magnesium alloy tailor-welded blanks Uniformity. Background technique [0002] Magnesium alloy is very suitable for portable electronic and electrical communication equipment due to its low density and good electromagnetic shielding properties. Control and reduce the harm to the human body. [0003] Magnesium alloy, as a light weight, strong and tough material with good rigidity, is used in aviation, spacecraft and missiles, which can increase the payload and flight distance, and reduce the service cycle and cost. Therefore, it began to be used in aviation equipment and other fields as early as World War II. For example, magnesium alloy pipe fitti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21D22/20B21D37/16B21D37/18
Inventor 王忠堂齐广霞梁海成刘劲松王芳李艳娟
Owner SHENYANG LIGONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap