Heavy metal welding protection glass

A heavy metal and electric welding technology, applied in goggles, optics, instruments, etc., can solve problems such as short service life, welder injury, and low safety performance

Inactive Publication Date: 2009-03-11
许昌天和焊接器材有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing welding protective lenses used on welding masks have always used transparent colorless glass as the preferred manufacturing material, which has the defects of low product safety performance, poor high temperature resistance and transmittance performance, and short service life, which brings great difficulties to electric welders. very serious bodily harm
There is also the use of black glass to solve the above-mentioned defects, but this kind of black glass has the defect that it is not resistant to ultraviolet rays and infrared rays, and it will also cause great physical harm to welders.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0006] Embodiment 1: The present invention is prepared from the following raw materials according to the weight in grams: 60 kilograms of quartz sand, 6 kilograms of ferric oxide, 1 kilogram of cerium oxide, 0.5 kilogram of cobalt oxide, 8 kilograms of soda ash, 3 kilograms of calcite, nickel oxide 1 kg, 2 kg of manganese powder.

Embodiment 2

[0007] Embodiment 2: The present invention is prepared from the following raw materials according to the weight in grams: 80 kilograms of quartz sand, 10 kilograms of ferric oxide, 4 kilograms of cerium oxide, 2 kilograms of cobalt oxide, 10 kilograms of soda ash, 5 kilograms of calcite, nickel oxide 2 kg, 5 kg of manganese powder.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
transmittivityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a heavy metal electric welding protective lens with uvioresistant and anti-infrared function used on a welding mask, which is prepared by the following material according to parts by weight: 60-80 parts of quartz sand, 6-10 parts of ferric oxide, 1-4 parts of cerium oxide, 0.5-2 parts of cobalt oxide, 8-10 parts of calcined soda, 3-5 parts of calcite, 1-2 parts of nickel oxide and 2-5 parts of manganese powder, and has the advantages of uvioresistant and anti-infrared. The invention can resist the infrared, the ultraviolet radiation and the harmful light, and visible light can be passed, simultaneously, the visible light of a welding object filtered by the lens of the invention can be comfortably observed by welder, the ultraviolet transmittance of the invention is between 313nm to 365nm, and the infrared transmittance is between 780nm to 1300nm or 1300nm to 2000nm, thus conforming with the requirement of national standard.

Description

Technical field: [0001] The invention relates to a heavy metal electric welding protective lens used on an electric welding mask with anti-ultraviolet and infrared functions. Background technique: [0002] The existing welding protective lenses used on welding masks have always used transparent colorless glass as the preferred manufacturing material, which has the defects of low product safety performance, poor high temperature resistance and transmittance performance, and short service life, which brings great difficulties to electric welders. There came a very great bodily injury. Also have to adopt black glass to solve the above-mentioned existing defect, but this black glass exists the defect that is not anti-ultraviolet, infrared ray, can bring very big bodily injury to electric welder equally. Invention content: [0003] The object of the present invention is to overcome the deficiencies in the prior art and provide a heavy metal electric welding protective lens wit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G02B1/02A61F9/02
Inventor 和新敬
Owner 许昌天和焊接器材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products