Method for preparing synthetic paper containing polysulfone amide precipitation fibers

A technology of polysulfone amide and precipitating fiber, which is applied in the directions of synthetic cellulose/non-cellulose material pulp/paper, fiber raw material processing, papermaking, etc., can solve the problems of insufficient strength retention rate, difficulty in applying insulating materials, etc. Dimensional stability, outstanding thermal oxidation resistance, and small weight loss

Active Publication Date: 2011-07-27
LONGPONT
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Patent application CN1834342 provides a kind of full meta-aramid fiber paper, which contains 5-95% of aramid 1313 chopped fibers and 5-95% of aramid 1313 precipitated fibers, because the meta-aramid fibers are mainly precipitated As a bonding fiber, the fiber has insufficient strength retention in high temperature environments, making it difficult to apply to a wider range of insulating materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing synthetic paper containing polysulfone amide precipitation fibers
  • Method for preparing synthetic paper containing polysulfone amide precipitation fibers
  • Method for preparing synthetic paper containing polysulfone amide precipitation fibers

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Prepare the present embodiment 1 synthetic fiber paper in the following proportions:

[0026] Aramid 1313 fiber (5-6mm) 55 parts by weight (hereinafter referred to as "parts")

[0027] 45 parts of polysulfone amide precipitated fiber

[0028] The aramid 1313 fiber with the above content is made into pulp in a fiber deflaking machine at a concentration of 1% by weight, and the polysulfone amide precipitated fiber is beaten by a refiner at a concentration of 2%, and the beating degree is controlled to be about 55°SR. slurry. After the two kinds of slurry are uniformly mixed in the batching tank, the papermaking pulp that can be added to the headbox of the papermaking wire is formed, and polyethylene oxide is added into the pulp stabilization box. The head of the slurry on the net is adjusted by the stock stabilizing box, and the slurry is evenly distributed on the paper forming wire in the headbox, and the excess slurry is overflowed to the white water pool. When the s...

Embodiment 2

[0033]Prepare the present embodiment 2 fiber papers in the following proportions:

[0034] Aramid 1313 fiber (5 ~ 6mm) 90 parts

[0035] 10 parts of polysulfone amide precipitated fiber

[0036] In this embodiment, the amount of aramid 1313 fiber and polysulfone amide fibridated fiber is adjusted. The preparation method of the fiber paper is the same as in Example 1, and the results obtained are shown in Table 2:

[0037] The physical and mechanical properties of table 2 fiber paper

[0038]

Embodiment 3

[0040] Prepare the present embodiment 3 fiber papers in the following proportions:

[0041] Aramid 1313 fiber (5 ~ 6mm) 15 parts

[0042] Polysulfone amide precipitated fiber 85 parts

[0043] This embodiment adjusts the consumption of aramid 1414 fiber and fibrid, the preparation method of fiber paper is the same as that of Example 1, and the results obtained are shown in Table 3:

[0044] The physical and mechanical properties of table 3 fiber paper

[0045]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention provides a synthetic fiber paper, which contains the following ingredients in parts of weight: 5-95 parts of structural fiber and 5-95 parts of splicing fibers, wherein, the structural fiber is polyisophthaloyl metaphenylene diamide fiber and the splicing fiber is polysulfonamide precipitated fiber. The synthetic fiber paper is produced by the following steps: the structural fiber and the splicing fiber are made into be formed by a wet method and hot-rolled to obtain the paper. The synthetic fiber paper provided by the invention has high intensity conservation rate under the high temperature, excellent paper-making overall properties compared with the insulation paper made of full para-fiber, meta-fiber and full polysulfonamide material, and is more suitable for the insulation requirement under high-temperature environment.

Description

technical field [0001] The invention relates to a synthetic fiber paper, in particular to a chemical fiber paper containing polysulfone amide precipitated fiber and a preparation method thereof. Background technique [0002] With aerospace, military, electronics, machinery and other industries that require high safety and lightness, high-performance aramid fiber has high strength, low deformation, high temperature resistance, chemical corrosion resistance, no fatigue reaction and Excellent insulation performance and many other characteristics have been widely used. Therefore, high-performance aramid fiber paper has also emerged as the times require. [0003] Existing aramid fibers are used for papermaking. For poly-p-phenylene terephthalamide fibers (aramid 1414 fibers), most of them use polyester or polyphenylene sulfide hot-melt fibers as bonding fibers; For polym-phenylene isophthalamide fibers (aramid 1313 fibers), aramid 1313 fibrids are basically used as bonding fiber...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H25/04D21H13/26D21F11/00
Inventor 衡沛之唐文勇陶世毅王丽萍
Owner LONGPONT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com