Method for producing recuperated yarn tube base paper by using waste slag and product thereof
A technology of bobbin base paper and waste residue, which is applied in the production of regenerated bobbin base paper and the field of producing regenerated bobbin base paper by using waste residue, which can solve the problems of affecting the strength of paper sheets, easy delamination of paper sheets, and poor interlayer bonding force, etc., to achieve The effect of improving the bonding strength between layers
Active Publication Date: 2010-12-22
JIAN GRP
View PDF0 Cites 4 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, this kind of production method, on the one hand, uses all waste paper as the raw material, and the production cost is relatively high. On the one hand, there is a problem of interlayer bonding of paper sheets in the copy forming method of using multiple cylinders, and the poor interlayer bonding force makes the paper sheets easy to separate. layer, which affects the sheet strength of the paper
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0024] According to the preparation process of [specific implementation method], when the ratio of raw materials is set as waste pulp residue: waste paper=40:60, the production quantity is 400g / m 2 The physical index of bobbin base paper can reach: thickness 0.6mm, tightness 0.80g / m 2 , interlayer bond strength 510j / m 2 , Longitudinal ring pressure index 23n.m / g.
Embodiment 2
[0026] According to the preparation process of [specific implementation method], when the ratio of raw materials is set as waste pulp residue: waste paper=60:40, the production quantity is 400g / m 2 The physical index of bobbin base paper can reach: thickness 0.6mm, tightness 0.76g / m 2 , interlayer bond strength 486j / m 2 , Longitudinal ring pressure index 21n.m / g.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| thickness | aaaaa | aaaaa |
Login to View More
Abstract
The invention relates to a manufacturing method which utilizes waste residue to produce regenerated yarn cop base paper and an obtained product thereof. The method comprises the following steps: the full stuff of processed waste slurry residue and the full stuff of processed waste paper are mixed according to proportion to carry out sand paper tube forming and then the regenerated yarn cop base paper is obtained. By adopting the method, waste paper resources can be saved, waste water treatment can be reduced, and the obtained regenerated yarn cop base paper has the advantages of low ration, good quality and the like.
Description
technical field [0001] The invention relates to a method for producing regenerated bobbin base paper, in particular to a method for producing regenerated bobbin base paper by using waste residue. The invention also relates to the regenerated bobbin base paper obtained by the method. Background technique [0002] Bobbin paper is an industrial technical paper used by chemical fiber equipment factories in the textile industry to make filament high-speed spinning copper cores. It not only requires high dry and wet strength, smoothness and wear resistance, but also must have the characteristics of oil resistance and water resistance, and it is required to be lint-free and deformation-free during high-speed polyester spinning after being rolled into a tube. Do not burst. Based on the above characteristics, the bobbin paper is required to have a certain physical strength and a high quantitative (usually 360-520g / m 2 ), there is no requirement for its appearance quality. Before ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): D21H11/14D21F1/70D21C5/02D21F11/00D21F11/12D21F11/02D21H23/06D21H21/16
CPCY02W30/64
Inventor 汤湧泉
Owner JIAN GRP