Dual cure formulations with components comprising uretdione groups

A technology of isocyanate and dimer, which is applied in the direction of polyurea/polyurethane adhesives, adhesives, polyester coatings, etc., can solve problems such as no coating, no effect on coating hardness and scratch resistance

Inactive Publication Date: 2009-06-24
EVONIK DEGUSSA GMBH
View PDF29 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The use of isocyanate dimer-containing components therein resulted in improved interlayer adhesion, but in this cited example, no effect on the hardness and scratch resistance of the coating (Examples 3, 4 and V2)
No examples are given of coating properties using only thermal curing without radiation curing (i.e. simulating shadowed areas)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

(A) IRGACURE 184 Photoinitiator, Ciba(E) ARALDITE PT 912 Cocatalyst, glycidyl ester, Huntsman (C1) Zinc acetylacetonate Cocatalyst, Aldrich (C2)

[0084] raw material product description, manufacturer TEAB Tetraethylammonium Benzoate, RSA Corp. (C) DBTL Dibutyltin dilaurate, catalyst, Aldrich

[0085] A) Production of radiation curable resins

[0086] A1) Polyester Production

[0087] Adipic acid (292 g) and butanediol (295 g) were melted in a 21 flask with a distillation head under nitrogen flow. When the temperature reaches 160°C, water starts to distill out. The temperature was continuously raised to 220°C over a period of 1 hour. After 4 hours at this temperature, the separation of water slowed down. 200 mg of FASCAT 4102 (transesterification catalyst from Arkema) were incorporated with stirring and the operation was continued under reduced pressure, which was adjusted during the reaction so that distillate produc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to dual cure formulations with components comprising uretdione groups. The present invention relates to novel formulations that can be cured thermally and by actinic radiation, referred to as dual cure formulations. Furthermore, the present invention relates to the use of the novel formulations that can be cured thermally and by actinic radiation for the production of pigmented and pigment-free paints and for adhesives and sealants.

Description

technical field [0001] The present invention relates to novel formulations which are thermally curable and which can be cured by means of actinic radiation, so-called dual-cure formulations. The invention also relates to the use of the novel thermally curable and actinic radiation-curable formulations for the production of colored or clear paints or adhesives and sealants. Background technique [0002] Formulations curable by actinic radiation are known. [0003] Ethylenically unsaturated prepolymers are described e.g. in P.K.T. Oldring (ed.), "Chemistry and Technology of UV-and EB-Formulation for Coatings, Inks and Paints", Vol. II, SITA Technology, London 1991, e.g. based on epoxy acrylic esters (pp. 31-68), urethane acrylates (pp. 73-123) and melamine acrylates (pp. 208-214). Such formulations are also frequently mentioned in the patent literature, examples that may be mentioned are JP 62110779 and EP 947 565 . [0004] Coating of metal substrates is a particular probl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D175/14C09J175/04C09J175/14C09K3/10C08J7/04C14C9/00D06M15/564C03C17/32
CPCC09D175/16C08G18/798D06M15/564C08G18/672D06M13/463C09D167/07C09D175/04D06M15/572D06M15/51D06M15/568D06M15/263D06M10/10C08J3/243C08G18/42C08L2666/14
Inventor E·斯派劳H·洛什
Owner EVONIK DEGUSSA GMBH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com