Amorphous alloy thermoforming apparatus and technique

An amorphous alloy, hot-press forming technology, applied in forging/pressing/hammer devices, forming tools, metal processing equipment, etc., can solve the problems of easy crystallization, low deformation rate and low processing efficiency of amorphous alloys

Active Publication Date: 2009-07-01
BYD CO LTD
View PDF0 Cites 45 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the embodiments of the present invention is to provide a hot-press forming device for amorphous alloys, which aims to solve the problem of long heating time, low d...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Amorphous alloy thermoforming apparatus and technique
  • Amorphous alloy thermoforming apparatus and technique

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] In order to make the technical problems, technical solutions and beneficial effects to be solved by the present invention clearer, the present invention will be further described in detail below in conjunction with the embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0015] figure 1 It shows an amorphous alloy hot press forming device provided by an embodiment of the present invention, including a closed chamber 1, and a mold set 2 located in the closed chamber 1. The mold set 2 includes an upper mold 21, a lower mold 22 and an upper mold and a lower mold. The forming die 23 between the dies 21, 22, the blank 100 is placed in the forming die 23. A valve body 3 is arranged on the airtight chamber 1, and the valve body 3 is connected with a vacuum system or a gas supply system (not shown in the figure), which can ensure that the entire hot pressing proce...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thermal conductivityaaaaaaaaaa
Thermal conductivityaaaaaaaaaa
Thermal conductivityaaaaaaaaaa
Login to view more

Abstract

The invention provides a device and a process for the hot pressing and molding of an amorphous alloy. The device is provided with a vacuum, inert gas or nitrogen gas protective environment, and a mould set and an induction heating coil positioned in the environment; the mould set comprises an upper mould, a lower mould and a molding mould; the induction heating coil is at least wound in a peripheral space of the molding mould and is not contacted with the molding mould; and the process sequentially comprises the following steps in the vacuum, inert gas or nitrogen gas protective environment: blank placement, induction heating, hot pressing and molding, cooling, and mould extraction. By adopting an induction heating mode, the process can rapidly concentrate on heating a molded blank to Tg temperature above, and carry out the hot pressing and molding within the temperature range between Tg and Tm or the Tm temperature above; a molding strain rate can reach between 10 and 10S; and the process has high processing efficiency and can effectively prevent crystallization of the amorphous alloy in the molding process within shorter temperature rise time.

Description

technical field [0001] The invention belongs to the technical field of amorphous alloy forming, and in particular relates to an amorphous alloy hot-press forming device and process. Background technique [0002] In recent years, with the deepening of research on the composition, structure and performance of bulk amorphous alloys, people have increasingly realized that the excellent physical, chemical, mechanical properties and precision formability of bulk amorphous alloys will make It has become a key material supporting high and new technologies such as precision machinery, information, aerospace devices, and national defense industries in the future. [0003] Compared with traditional crystalline alloy materials, bulk amorphous alloy materials have obvious advantages in many aspects of performance, and have more excellent mechanical properties. They are not only greatly superior in strength, elasticity, toughness, hardness, etc. Traditional metal materials are not inferi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21D22/00B21D37/16B21D37/10B21D37/01B21J5/00B21J1/06B21J13/02
Inventor 马志军张法亮
Owner BYD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap