Method for selection and preparation of raw materials of high-strength suspension porcelain insulator glaze

A porcelain insulator and raw material technology, applied in the field of selection and preparation of glaze raw materials for high-strength suspension porcelain insulators, can solve problems such as inconsistent selection, achieve good fluidity, quality assurance, and improve electromechanical performance and insulation performance

Inactive Publication Date: 2009-08-26
INST OF GEOCHEM CHINESE ACADEMY OF SCI +1
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In view of the defect that the selection of raw materials for the glaze of the electric porcelain body is not uniform, the purpose of the present invention is to provide a method for selecting and preparing the raw materials of the glaze for high-strength suspension porcelain insulators

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for selection and preparation of raw materials of high-strength suspension porcelain insulator glaze

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] Following is the concrete process step of implementing the present invention:

[0020] First, choose kaolinite clay 10-15%, talc 10-15%, feldspar 25-35%, refined quartz 25-35%, carbonate 5-10%, ordinary porcelain powder 1-8%, water glass 0.1-0.5%, calcined bauxite 10-15%. The particle size of the clay raw material is 20-40 mesh, and the particle size of other raw materials is 180-200 mesh. After mixing evenly, ball milling, and then component analysis. Its compositional analysis data and particle size are expressed as follows:

[0021] Calculation of chemical composition (%)

[0022] SiO 2

[0023] Particle size analysis

[0024] Micron

[0025] Specifically, the preparation is carried out according to the following process steps. The first step: raw material preparation, select kaolinite clay 10-15%, talc 10-15%, feldspar 25-35%, refined quartz 25-35%, carbonate 5% ~10%, ordinary porcelain powder 1~8%, water glass 0.1~0.5%, calcined bauxite 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for the selection and the preparation of the raw materials of a high-strength suspension porcelain insulator glaze. The raw materials comprise kaolinite type clay, talcum, feldspar, refined quartz, carbonate, porcelain powder, water glass and calcined alumina. The invention is characterized in that the kaolinite type clay is 10 to 15%, the talcum is 10 to 15%, the feldspar is 25 to 35%, the refined quartz is 25 to 35%, the carbonate is 5 to 10%, the porcelain powder is 1 to 8%, the water glass is 0.1 to 0.5% and the calcined alumina is 10 to 15%. The particle size of each clay raw material is 20 to 40 mushes, the particle size of other raw materials is 180 to 200 mushes. The bending strength of porcelain blank can be improved by 25 to 40% after being glazed by the glaze, the sintering temperature of the porcelain insulator after being glazed is 1200 to 1350 DEG C.

Description

technical field [0001] The invention relates to an aluminosilicate material, which is particularly suitable for the selection and preparation of high-strength suspension porcelain insulator glaze raw materials for AC transmission lines. Background technique [0002] With the implementation of the strategy of "power transmission from west to east, national interconnection, and mutual supply between north and south" in my country, the country attaches great importance to the development of ultra-high voltage and ultra-high voltage technology and the localization of supporting equipment. In the future, my country's high-tonnage, large-capacity long-distance transmission lines will More and more, the future demand for matching suspension porcelain insulators for transmission lines will also increase. According to statistics from relevant departments: the annual domestic demand for suspension porcelain insulators is about 10 million tons. [0003] Suspension porcelain insulator is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86
Inventor 龚国洪伍正平谢玉敏尹中举金行赵莽原代振华尹祚莹王志宏龚翼刘世荣
Owner INST OF GEOCHEM CHINESE ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap