Solvent-resistance polystyrene ternary alloy material for refrigerator inner liner plates and preparation method and application thereof

A polystyrene and refrigerator liner technology, which is applied in applications, household refrigeration devices, chemical instruments and methods, etc., can solve the problems of unstable grafting rate, unstable compatibility, and increased production costs of grafted materials. Achieve good hot-melt processing performance, excellent solvent resistance, and rapid delivery

Active Publication Date: 2009-09-30
QINGDAO HAIER NEW MATERIAL R&D CO LTD
View PDF5 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the lining material can also improve solvent resistance, the formula is relatively complicated, which also increases the production cost to a certain extent. The grafted compatibilizer is irritating when it is heated, melted, extruded, granulated and extruded. The odor of the maleic anhydride residue, and the compatibility is actually unstable due to the instability of the grafting rate of the graft

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solvent-resistance polystyrene ternary alloy material for refrigerator inner liner plates and preparation method and application thereof
  • Solvent-resistance polystyrene ternary alloy material for refrigerator inner liner plates and preparation method and application thereof
  • Solvent-resistance polystyrene ternary alloy material for refrigerator inner liner plates and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The solvent-resistant polystyrene ternary alloy material for the refrigerator liner plate of the present embodiment is composed of 65% high-impact polystyrene, 20% linear low-density polyethylene, and 14% ethylene-butadiene-styrene copolymer phase Composite agent, 0.5% antioxidant 1010 and 0.5% calcium stearate.

[0036] Among them, high-impact polystyrene is 495F produced by BASF, MI is 12g / 10min (200℃ / 5kg), Izod impact strength is 110J / m, linear low-density polyethylene MI is 9g / 10min (190℃ / 5kg), ethylene-butadiene-styrene copolymer is a block copolymer, wherein the ethylene content is 25%.

[0037] The solvent-resistant polystyrene ternary alloy material used for the refrigerator liner plate in this embodiment is firstly added to a high-speed mixer in proportion to each component and mixed at a high speed for 3 minutes, and then subjected to twin-screw extrusion at 200±10°C. Extruded out of the machine, the strips are cooled in the water tank, and then cut into all...

Embodiment 2

[0041] The solvent-resistant polystyrene ternary alloy material for the refrigerator liner plate of the present embodiment is composed of 35% high-impact polystyrene, 40% linear low-density polyethylene, and 24.3% ethylene-butadiene-styrene copolymer phase Composite agent, 0.1% antioxidant 168 and 0.6% calcium stearate.

[0042] Among them, the high-impact polystyrene is 1300 produced by Dow in the United States, the MI is 7.5g / 10min (200°C / 5kg), the Izod impact strength is 100J / m, and the MI of linear low-density polyethylene is 6g / 10min (190°C). ℃ / 5kg), ethylene-butadiene-styrene copolymer is a block copolymer, wherein the ethylene content is 35%.

[0043] The solvent-resistant polystyrene ternary alloy material for the refrigerator liner plate in this embodiment is firstly added to the high-speed mixer in proportion to the high-speed mixing for 2 minutes, and then subjected to twin-screw extrusion at 180±10°C. Extruded out of the machine, the strips are cooled in the water...

Embodiment 3

[0045] The solvent-resistant polystyrene ternary alloy material for the refrigerator liner plate of the present embodiment is composed of 55% high-impact polystyrene, 35% linear low-density polyethylene, and 9.5% ethylene-butadiene-styrene copolymer phase Composite agent, 0.2% antioxidant 1076 and 0.3% calcium stearate.

[0046] Among them, the high-impact polystyrene is 476L produced by BASF, the MI is 4g / 10min (200℃ / 5kg), the Izod impact strength is 80J / m, and the MI of linear low-density polyethylene is 2g / 10min (190℃ / 5kg). ), ethylene-butadiene-styrene copolymer is a block copolymer, wherein the ethylene content is 30%.

[0047] The solvent-resistant polystyrene ternary alloy material for the refrigerator liner plate in this embodiment is firstly added to the high-speed mixer in proportion to the high-speed mixing for 1 minute, and then extruded by twin-screw at 210±10°C. Extruded out of the machine, the strips are cooled in the water tank, and then cut into alloy product...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention provides a solvent-resistance polystyrene ternary alloy material used for refrigerator inner liner plates. The solvent-resistance polystyrene ternary alloy material comprises 20 to 65 percent of high-impact polystyrene, 15 to 60 percent of linear low-density polyethylene, 5 to 25 percent of ethane-butadiene-styrol copolymer compatilizer, 0.1 to 0.6 percent of antioxidant and 0.1 to 0.6 percent of calcium stearate. The invention also provides a preparation method and an application of the alloy material. The polyethylene has excellent solvent-resistance, the polystyrene has good mechanical strength, and the invention enables the polyethylene and the polythene to be mixed into an interpenetrating network structure through a special solvent polymer to form stable polymer alloy, therefore, the invention not only retains the mechanical property of the polystyrene but also has the excellent solvent-resistance of the polyethylene simultaneously, the solvent-resistance polystyrene product widely applied to the refrigerator inner liner plates is obtained, the material cost of the refrigerator inner liner plates is reduced, and the refrigerator inner liner plate material with stable supply of goods and quick delivery is provided.

Description

technical field [0001] The invention relates to a polystyrene alloy material, in particular to a solvent-resistant polystyrene ternary alloy material for a refrigerator liner plate, a preparation method and application thereof. Background technique [0002] Polystyrene (Polystyrene in English, referred to as PS) is a colorless and transparent thermoplastic. High-impact polystyrene is an impact-resistant polystyrene produced by adding polybutyl rubber particles to polystyrene. Styrene products are opaque and slightly white. This polystyrene product is connected with polystyrene and rubber particles by adding micron-sized rubber particles and grafting. [0003] An obvious disadvantage of polystyrene is that it has poor solvent resistance, can be dissolved by a variety of organic solvents, and will be corroded by strong acids and alkalis, and is not resistant to grease. [0004] Everyone is familiar with refrigerators, but little is known about the materials used to make refri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/06C08L23/06C08K5/098C08K5/13C08K5/524C08K5/36F25D23/06B29B9/12B29C47/92B32B5/18B32B15/095B32B27/08C08L25/08B29C48/92
CPCB29C48/92B29C2948/92704B29C2948/92895
Inventor 金道谟蒿文朋王立锋朱胜全李巍巍
Owner QINGDAO HAIER NEW MATERIAL R&D CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap